具有全珠光体组织的65Mn钢在650℃以C方式等径弯曲通道变形(ECAP)后,珠光体组织中的渗碳体片层以周期性的弯曲变形、周期性的剪切变形、剪切断裂等形式协调ECAP的强烈塑性变形.渗碳体表现出很强的塑性变形能力,在其内部导入了大量的晶体缺陷,为渗碳体的球化打下了能量基础.变形五道次后,片层状的珠光体组织演变成了超细的渗碳体颗粒均匀分布于铁素体基体的组织.铁素体基体为均匀的等轴晶,平均晶粒大小为～0.3 μm.渗碳体的球化可能以两种机制进行:破碎渗碳体片的非均匀长大(Ostwald熟化)和细小球状渗碳体颗粒的形核长大.
参考文献
| [1] | D.H.Shin, B.C.Kim, Y.S.Kim, K.T.Park, Acta Mater., 48, 3245(2000) |
| [2] | D.H.Shin, Y.S.Kim, J.Kim, K.T.Park, Acta Mater., 49, 1285(2001) |
| [3] | D.H.Shin, B.C.Kim, Y.S.Kim, K.T.Park, Acta Mater., 48, 2247(2000) |
| [4] | K.T.Park, Y.S.Kim, J.G.Lee, D.H.Shin, Mater. Sci. Eng., A293, 165(2000) |
| [5] | D.H.Shin, C.W.Seo, J.Kim, K.T.Park, W.Y.Choo, Scripta Mater., 42, 695(2000) |
| [6] | Y.Fukuda, K.Oh-ishi, Z.Horita, T.G.Langdon, Acta Mater., 50, 1359(2002) |
| [7] | S.A.Hackeny, G.J.Shiflet, Acta Metal., 35, 1019(1987) |
| [8] | M.Dollar, I.M.Bernstein, A.W.Thompson, Acta Metal., 36, 311(1988) |
| [9] | D.A.Porter, K.E.Easterling, Acta Metal., 26, 1405(1978) |
| [10] | M.H.Hong, W.T.Reynodls, Jr., T.Tarui, K.Hono, Metal. Mater. Trans., 30A, 717(1999) |
| [11] | HU Guangli, XIE Xiwen, Thermal Treatment of Steel (Xi'an, Northwestern Polytechnical University Press,1993) p.195(胡光立,谢希文,钢的热处理(西安,西北工业大学出版社,1993)p.195) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%