用气相氧化法合成出具有纳米棒-线结构的ZnO纳米材料.扫描电子显微镜(SEM)、透射电子显微镜(TEM)观察和X射线衍射谱(XRD)的分析表明:四角状ZnO纳米材料具有六方纤锌矿晶体结构,在棒-线纳米结构中,每个角的长度为1～2 μm,纳米棒的直径为100～200 nm,纳米线的直径约为30 nm.用气-固(VS)生长机制解释了棒-线纳米结构的形成.与ZnO大块材料不同,四角状ZnO纳米棒-纳米线材料在室温下具有～380 nm波长的紫外发射和～520 nm波长的绿光发射,其机理是晶体中杂质与结构缺陷少,以及与其纳米尺度相联系的量子限域效应.
参考文献
| [1] | Y.Li, G.W.Meng, L.D.Zhang, Appl. Phys. Lett., 76(15), 2011(2000) |
| [2] | M.H.Huang, Y.Y.Wu, H.Feick, N.Tran, E.Weber, P.D.Yang, Adv. Mater., 13(2), 113(2001) |
| [3] | M.H.Huang, S.Mao, H.Feick, H.Q.Yan, Y.Y.Wu, H.Kind, E.Weber, R.Russo, P.D.Yang, Science, 292, 1897(2001) |
| [4] | Y.W.Wang, L.D.Zhang, G.Z.Wang, X.S.Peng, Z.Q.Chu, C.H.Liang, J. Crystal. Growth, 234, 171(2002) |
| [5] | J.S.Lee, K.Park, M.I.Kang, I.W.Park, S.W.Kim, W.K.Cho, H.S.Han, S.Kim, J. Crystal. Growth, 254,423(2003) |
| [6] | Z.W.Pan, Z.Rong. Dai, Z.L.Wang, Science, 291, 1947(2001) |
| [7] | W.I.Park, G.C.Yi, M.Y.Kim, S.J.Pennycook, Adv. Mater, 14(24), 1841(2002) |
| [8] | J.Q.Hu, Q.Li, X.M.Meng, C.S.Lee, S.T.Lee, Chem. Mater, 15,305(2002) |
| [9] | P.X.Gao, Z.L.Wang, J. Phys. Chem. B, 106(49), 12653(2002) |
| [10] | J.G.Wen, J.Y.Lao, D.Z.Wang, T.M.Kyaw, Y.L.Foo, Z.F.Ren, Chem. Phys. Lett., 372, 717(2003) |
| [11] | J.Y.Lao, J.Y.Huang, D.Z.Wang, Z.F.Ren, Nano. Lett., 3(2), 235(2003) |
| [12] | Y.Dai, Y.Zhang, Q.K.Li, C.W.Nan, Chem. Phys. Letter, 358, 83(2002) |
| [13] | P.D.Yang, C.M.Liber, J. Mater. Res., 12, 2981(1997) |
| [14] | M.Kitano, T.Hambe, S.Maeda, J. Crystal. Growth, 108, 277(1991) |
| [15] | H.I.Wanaga, M.Fujii, S.Takeuchi, J. Crystal. Growth, 134, 275(1993) |
| [16] | W.J.Li, E.W.Shi, W.Z.Zhong, Z.W.Yin, J. Crystal. Growth, 203, 186(1999) |
| [17] | D.M.Bagnall, Y.F.Chen, Z.Zhu, T.Yao, S.Koyama, M.Y.Shen, T.Goto, Appl. Phys. Lett., 70(17),2230(1997) |
| [18] | C.Kong, D.P. Yu, B.Zhang, W.Fang, S.Q.Feng, Appl. Phys. Lett, 78(4), 407(2001) |
| [19] | K.Vanheusden, W.L.Warren, C.H.Seager, D.R.Tallant, J.A.Voigt, B.E.Gnade, J. Appl. Phys., 79,7983(1996) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%