采用喷射轧制工艺制备了钢/Al-8.5Pb-4Si-Cu-0.5Sn复合轴瓦带材,分析了所制备材料的组织及性能.结果表明,用喷射轧制工艺制备的轴瓦合金Al-Si基体中分布有均匀细小的Pb相粒子,经过50%变形量的轧制和在320℃后续退火5h的处理,在复合轴瓦带材的界面处发生了合金元素的扩散,形成了良好的冶金结合层,界面强度高,剪切强度达到72MPa.用喷射轧制工艺制备的轴瓦合金具有良好的耐磨性能.
参考文献
| [1] | J.Z.Zhao,L.Ratke,Modeling Simul.Sci.Eng.,6,123(1998) |
| [2] | A.Sharma,T.V.Rajan,Wear,197,105(1996) |
| [3] | Collycar.John,The Chinese Journal of Nonferrous Metals(中国有色金属学报),3(4),88(1993) |
| [4] | S.Mohan,V.AgarWala,S.Ray,Wear,140,83(1990) |
| [5] | K.Lepper,M.James,J.Chashechkina,Wear,203,46(1997) |
| [6] | SUN Daren(孙大仁),LIU Yongbing(刘勇兵),AN Jian(安健),LU You(陆有),CAO Zhanyi(曹占义),The Chinese Journal of Nonferrous Metals(中国有色金属学报),8(Suppl.1),141(1998) |
| [7] | B.Prinz,A.Romero,In:Immiscible Liquid Metals and Organics,L.Ratke ed.,(DGM-Informations gesellschaft,Oberursel,Germany,1993)p.281 |
| [8] | T.Berrenberg,In:Immiscible Liquid Metals and Organics,L.Ratke ed.,(DGM-Informationsgesellschaft,Oberursel,Germany,1993)p.299 |
| [9] | Y.Ogita,Y.Ido,M.Sakamoto,Metallurgy of Powder Research,2,37(1991) |
| [10] | A.R.E.Singer,Metals and Materials,4(6),246(1970) |
| [11] | P.S.Grant,Spray Forming,Prog.Mater.Sci.,39,497(1995) |
| [12] | A.Updhyaya,N.S.Mishra,S.N.Ojha,Journal of Material Science,32,3227(1997) |
| [13] | LI Xiaoxue(李晓学),LIU Yong(刘勇),SUN Jiyue(孙继跃),CUI Hua(崔华),DUAN Xianjin(段先进),ZHANG Jishan(张济山),The Chinese Journal of Nonferrous Metals(中国有色金属学报),9(Suppl 1),106(1999) |
| [14] | YU Jiuming(于九明),YU Changsheng(于长生),ZHU Quan(朱泉),Journal of Northeastern University(Natural Science)(东北大学学报(自然科学版)),16(5),491(1995) |
| [15] | ZHANG Caipei(张彩碚),CUI Jianzhong(崔建忠),Acta Metallurgica Sinica(金属学报),35,113(1998) |
| [16] | D.Pan,K.Gao,J.Yu,Materials Science and Technology,5(9),934(1989) |
| [17] | ZHU Quan(朱泉),PAN Dawei(潘大炜),ZHANG Wenqi(张文奇),Steel Rolling(轧钢),4,19(1989) |
| [18] | S.N.Ojha,A.K.Tripathi,S.N.Singh,Powder Metallurgy Inter.,25(2),65(1993) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%