在Cr-Mn-N奥氏体钢空蚀损伤的样品表面出现了高温η-Ni3Ti相和尺寸约为30nm的纳米晶.前者是空蚀过程中的热效应所致,后者则是机械和热效应共同作用的结果.推测在Cr-Mn-N奥氏体钢空蚀试验时可能出现1100K左右的瞬时高温.发展抗空蚀材料除了应考虑常温组织和性能外,还应考虑材料的高温组织、性能和冷热疲劳性能
参考文献
| [1] | 陆力,水机磨蚀,7,11(1991)(LU Li,Abrasion and Cavitation in Hydraulic Machinery,7,11(1991)) |
| [2] | 徐学豪,寇希颜,水机磨蚀,35,38(1990)(XU Xuehao,KOU Xiyan,Abrasion and Cavitation in Hydraulic Machinery,35,38(1990)) |
| [3] | 苏虹,水机磨蚀,86(1985)(SU Hong,Abrasion and Cavitation in Hydraulic Machinery,86(1985)) |
| [4] | P.D.Jarman,K.J.Taylor,Brit.Jr.Appl.Phys,,321(1964) |
| [5] | R.T Knapp,J.W.Daily,F.G.Hammit,Cavitation,水利水电科学研究院译(北京,水利出版社,1981)p.98(R.T.Knapp,J.W.Daily,F.G.Hannit,Cavitation,98,Translated by Chinese Academy of Hydraulic-power(Beijing,Hydraulic Press,1981)) |
| [6] | 王者昌,梁亚南,郑凤珍,梁殿清,白良谋,姚启鹏,于江城,GB1堆焊金属磨蚀试验研究,第12届中国水电设备学术讨论会论文集,四川省水力发电工程学会编辑,(重庆,四川省水力发电工程学会,1995)p.316(WANG Zechang, LIANG Yanan, ZHENG Fengzhen, LIANG Dianqing, BAI Liangmou, YAO Qipeng, YU Jiangcheng, Abrasion and Cavitation Erosion Investigation of GB1Overlaid Metal, 316, Proceeding of the 12th Symposium on Chinese Hydraulic Power Equipment) |
| [7] | T.Okada, Y.Iwai, S.Hattor, N.Tanimura, Wear, 184, 231(1995) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%