研究了用溶胶-凝胶(sol-gel)方法在LaAlO3(100)衬底上制备的La1-xCaxMn1.03O3外延薄膜的磁电阻效应.x在0.2～0.621范围内变化,外延薄膜的电阻率与温度的关系从类半导体行为向金属导电行为转变.在x≥0.5的4个样品中没有发现电荷有序绝缘体(COI)和反铁磁绝缘体(AFI)现象.x=0.2样品在1.5T磁场下磁电阻率MR的最大值为104%、磁转变温度为230K.
参考文献
| [1] | R.Von Helmolt, J.Wecker, B.Holzapfel, L.Schultz and K.Samwer, Phys.Rev. Lett., 71, 2331(1993) |
| [2] | 蔡建旺,赵见高,詹文山,沈保根,物理学进展,17(2),119(1997) |
| [3] | 戴道生,熊光成,吴思诚,物理学进展,17(2),202(1997) |
| [4] | C.N.R.Rao, A.K.Cheetham, R.Mahesh, Chem. Mater., 8(10), 2421(1996) |
| [5] | A.J.Millis, J.Appl. Phys., 83, 1588(1998) |
| [6] | A.S.Alexandrov, A.M.Bratkovsky, Phys. Rev. Lett., 82(1), 141(1999) |
| [7] | A.J.Millis, Nature, 392, 147(1998) |
| [8] | P.Schiffer, A.P. Ramirez, W.Bao, S.W.Cheong, Phys. Rev. Lett., 75, 3336(1995) |
| [9] | Y.Tomioka, A.Asamitsu, H.Kuwahara, Y.Moritomo, Y.Tokura, Phys. Rev. B, 53, R1689(1996) |
| [10] | Seung-Young Bae, Shan Xiang Wang, Appl. Phys. Lett., 69(1), 121(1996) |
| [11] | J.A.M.Van Roosmalen, P. Van Vlaanderen, E.H.P. Cordfunke, W.L.Ijdo, D.J.W.Ijdo, Journal of Solid State Chemistry, 114, 516(1995) |
| [12] | X.D.Wang, X.G.Zhang, Phys.Rev.Lett., 82, 4276(1999) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%