对分别加入4种稀释剂的双酚A环氧树脂和酚醛环氧树脂的电子束辐射固化性能进行了研究.分析了稀释剂种类及含量对环氧树脂体系辐射产物的固化度、固化均匀性、固化区域大小及其动态力学性能的影响规律.结果表明:电子束固化环氧树脂体系中加入稀释剂后,辐射产物的固化度、玻璃化转变温度及储能模量有所下降,但固化均匀性得到提高;加入稀释剂的环氧树脂电子束固化区域的厚度均小于未加稀释剂树脂,而底面直径却大于未加稀释剂树脂;随着树脂中实际稀释剂含量的增加,电子束固化环氧树脂固化度逐渐降低,固化层厚度减小,固化区域的底面直径先增加后减小.
参考文献
[1] | Berejka A J,Eberle C.Electron beam curing of composites in North America[J].Radiation Physics and Chemistry,2002,63:551-556. |
[2] | Zhang Zuoguang,Li Yubin,Wu Yan,et al.Exothermic effect in the process of electron-beam curing of epoxy resins[J].Journal of Applied Polymer Science,2004,94(5):2217-2222. |
[3] | Zhang Zuoguang,Sui Gang,Zhong Weihong,et al.Effect of heat treatment on thermomechanical properties of electron beam-cured epoxy resins[J].Polymer and Polymer Composites,2002,10(6):467-480. |
[4] | Zsigmond B,Halasz L,Czvikovszky T.Electron beam processing of carbon fibre reinforced braided composites[J].Radiation Physics and Chemistry,2003,67(3/4):441-445. |
[5] | Korenev S.Electron beam curing of composites[J].Vacuum,2001,62:233-236. |
[6] | 刘玉文,张志谦,黄玉东,包建文.电子束固化复合材料界面[J].复合材料学报,2002,19(3):16-20.Liu Yuwen,Zhang Zhiqian,Huang Yudong,Bao Jianwen.Interface of electron beam cured carbon fiber reinforced composites[J].Acta Materiae Compositae Sinica,2002,19(3):16-20. |
[7] | 李红霞,张佐光,李玉彬.纳米SiO2对双酚A环氧树脂电子束固化特性的影响[J].复合材料学报,2005,22(4):11-16.Li Hongxia,Zhang Zuoguang,Li Yubin.Effect of nano-SiO2 on electron beam curing characteristics of bisphenol A epoxy resin system[J].Acta Materiae Compositae Sinica,2005,22(4):11-16. |
[8] | Ghosh N N,Palmese G R.Electron-beam curing of epoxy resins:Effect of alcohols on cationic polymerization[J].Bulletin of Materials Science,2005,28(6):603-607. |
[9] | Li Yuntao,Morgan R J,Tschen F,Sue H J,Lopata V.Electron-beam curing of bismaleimide-reactive diluent resins[J].Journal of Applied Polymer Science,2004,94(6):2407-2416. |
[10] | Crivello J V,Fan M,Bi D.The electron beam-induced cationic polymerization of epoxy resins[J].Journal of Polymer Science,1992,44:9-16. |
[11] | Ribeiro R,Morgan R J,Bonnaud L,Lu J,Sue H J,Choi J,Lopata V.Characterization of the electron beam curing of cationic polymerization of diglycidylether of bisphenol A epoxy resin[J].Journal of Composite Materials,2005,39(16):1433-1448. |
[12] | Anseth K S,Bowman C N,Peppas N A.Dynamic mechanical studies of the glass transition temperature of photopolymerized multifunctional acrylates[J].Polymer Bulletin,1993,31:229-233. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%