采用新颖的纳米掺杂工艺成功制备了BaTiO3基MLCC超细抗还原瓷料.TG-DTA、XRD、TEM分析表明,通过水基溶胶-凝胶法合成了高分散、高活性的纳米掺杂剂,平均粒度约40.2 nm.根据传统工艺与纳米掺杂工艺的比较,对纳米掺杂机理进行了研究.实验发现,由于纳米粉体的特殊效应,纳米掺杂工艺能更有效地提高掺杂原子的取代改性作用,从而更显著地改善瓷料的微观结构和宏观介电性能.样品经测试符合EIAX7R/X8R标准,其介电常数K25℃>2800、介质损耗tanδ<1.0%、绝缘电阻率IR=1012Ω·cm、平均晶粒尺寸Gav≈0.3 μm.
参考文献
[1] | Kishi H, Mizuno Y, Chazono H. Base metal electrode-multilayer ceramic capacitors: Past, present and future perspectives[J]. Jpn J ApplPhys, 2003, 42(1): 1-15. |
[2] | Kumazawa H, Kagimoto T, Kawabata A. Preparation of barium titanate ultrafine particles from amorphous titania by a hydrothermal method and specific dielectric constants of sin tered discs of the prepared particles [J]. J Mater Sci, 1996,31(10): 2599-2602. |
[3] | 高家化,沈志坚,丁子上.陶瓷基纳米复合材料[J].复合材料学报,1994,11(1):1-7.Gao J H, Shen Z J, Ding Z S. Ceramic-matrix nanocomposite [J]. Acta Materiae Compositae Sinica, 1994, 11(1): 1-7. |
[4] | 王昕,孙康宁,尹衍升,等.纳米复合陶瓷材料研究进展[J].复合材料学报,1999,16(1):105-110.Wang X, Sun K N, Yin Y S, et al. Progress of study on ce ramic-matrix nanocomposites [J]. Acta Materiae Compositae Sinica, 1999, 16(1): 105-110. |
[5] | Fang T T, Hsieh H L, Shiau F S. Effect of pore morphology and grain size on the dielectric properties and tetragonal-cubic phase transition of high purity barium titanate [J]. J Am Ceram Soc, 1993, 76(5): 1205-1211. |
[6] | Hennings D, Rosenstein G. Temperature-stable dielectrics based on chemically inhomogeneous BaTiO3 [J]. J Am Ceram Soc, 1984, 67(4): 249-254. |
[7] | Chazono H, Fujimoto M. Sintering characteristics and formation mechanisms of "core-shell" structure in BaTiO3 Nb2O5Co3O5 ternary system [J]. Jpn J Appl Phys, 1995, 34(9):5354-5359. |
[8] | Kishi H, Okino Y, Honda M, et al. The Effect of MgO and rare-earth oxide on formation behavior of core-shell structure in BaTiO3 [J]. Jpn J Appl Phys, 1997, 36(9): 5954-5957. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%