研究了在溶胶-凝胶法原位制备纳米二氧化硅复合材料过程中硅烷偶联剂与纳米二氧化硅间的作用机理,硅烷偶联剂量的变化对机理的影响以及对在环氧树脂清漆中应用性能的影响.结果表明:溶胶凝胶法纳米二氧化硅复合材料的形成机理是纳米二氧化硅表面的物理吸附水和硅羟基被硅烷偶联剂的有机部分所代替,生成分散均匀的纳米复合材料.当硅烷偶联剂的用量适当时该复合材料在环氧树脂清漆中具有良好的应用性能,表现出纳米材料特有的既增强又增韧特性,有很好的应用前景.
参考文献
| [1] | 徐国财, 张立德. 纳米复合材料 [M]. 北京:化学工业出版社,2002. 3-18. |
| [2] | Zhuravlev L T. The surface chemistry of amorphous silica [J]. Colloids and Surfaces,2000,173:1-38. |
| [3] | John T. Silane coupling agents for enhanced silica performance [J]. Rubber World, 1998,9: 38-47. |
| [4] | Wu W, Chen J F, Shao L, et al. Study on polymer grafting modification of the surface of nano silicon dioxide [J]. Journal of Beijing University of Science and Technology, 2002, 9(6): 426-430. |
| [5] | Nassar E J, Neri C R, Calefi P S, et al. Functionalized silica synthesized by sol-gel process [J]. Journal of Non-Crystalline Solids, 1999, 247: 124-128. |
| [6] | Stolarski M, Walendziewski J, Pniak M S B. Synthesis and characteristic of silica aerogels [J]. Applied Catalysis A: General, 1999, 177: 139-148. |
| [7] | Park S K, Kim K D, Kim H T. Preparation of silica nanoparticles: determination of the optimal synthesis conditions for small and uniform particles [J]. Colloids and Surfaces A: Physicochem Eng Aspects, 2002, 197: 7-17. |
| [8] | 尚修勇,朱子康,印杰,等. 偶联剂对PI/SiO2纳米复合材料形态结构与性能的影响-Ⅰ [J]. 复合材料学报,2000, 17(4):15-19. |
| [9] | 容智敏,章明秋,郑永祥,等. 纳米SiO2增韧增强聚丙烯的界面效应与逾渗行为 [J]. 复合材料学报,2002,19(1): 1-4. |
| [10] | 华仲强,林永渭,吴叙勤. 硅烷偶联剂/二氧化硅界面层的表征研究 [J]. 复合材料学报, 1988, 5(3): 47-54. |
| [11] | 熊传溪,闻荻江,皮正杰. 超微细Al2O3增韧增强聚苯乙烯的研究 [J]. 高分子材料科学与工程,1994, 10(4): 69-73. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%