采用三种不同的有机物马来酸酐、油酸、2,2'-联吡啶作为配位体与SrAl2O4:Eu2+,Dy3+发光粉进行了配位包覆形成有机-无机杂化发光材料.通过IR、XRD、SEM、荧光光谱分析和耐水性测试结果表明:包覆层由三种有机物通过O或N原子与发光粉晶体表面的Sr2+配位键合而成,包覆后晶体结构和荧光光谱峰形和峰位没改变,发光强度降低,表面粗糙度变大,在水中的稳定性增强,其中马来酸酐是最好的配位体,包覆后荧光强度和余辉时间分别为包覆前的97%和95%.
参考文献
| [1] | Murayama Y,Takeuchi N,Aoki Y,et al.Phosphorescent phosphor,US Patent,5686022,1997. |
| [2] | Qiu J Y,Hirao K.Solid State Communications.1998,106 (12):795-798. |
| [3] | Bodi J A,Phillips T L.Daylight/night glow colored phosphorescent plastic compositions and articles.WO27908,2000. |
| [4] | Van D,Debra M.Tintable Luminescence Paint,US Patent,6359048,2002. |
| [5] | Lin Y,Zhang Z,Zhang F,et al.Materials Chemistry and Physics,2000,65:103-106. |
| [6] | Xingdong Lu.Materials Chemistry and Physics.2005,93:526-530. |
| [7] | 吕兴栋,舒万艮,谭爱东,等(LU Xing-Dong,et al).无机材料学报(Journal of Inorganic Materials),2004,19(6):1373-1378. |
| [8] | 孙中新,刘应亮,黄浪欢,等.化学建材,2004,(4):26-28. |
| [9] | 郭崇峰,吕玉华,苏锵.中山大学学报(自然科学版),2003,42(6):47-50. |
| [10] | Yang H,Wang X J,Duan G H,et al.Materials Letters.,2004,58:2374-2379. |
| [11] | Maruwa Kogyo Kk.Hydrophobic phosphorescent material[P],JP09003449,1997. |
| [12] | Hitachi Chem Co Ltd.Surface treated fluorescent material,JP Patent,09125056,1997. |
| [13] | 侯佩民,刘福长,郭焱,等.水性蓄能发光涂料[P],CN1434088,2003. |
| [14] | 张玉军,郎军昌,朱仲力,等.一种水性丙烯酸蓄能发光涂料及其制备方法,CN1288031,2001. |
| [15] | 吕兴栋,舒万艮.应用化学,2005,22(6):638-642. |
| [16] | 中西香尔,PH 索罗曼.红外光谱分析100例.北京:科学出版社,1984.18. |
| [17] | 中本一雄.无机和配位化合物的红外拉曼光谱(中译本).北京:化工出版社,1986.235. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%