研究了不同V5+含量Mg4(SbNb1-xVx)O9[MSNV,0.05≤x≤0.3]系陶瓷的烧结特性、微观结构和微波介电性能.结果表明:一定量V5+取代能够明显降低该陶瓷的烧结温度.在所有组成范围内,XRD显示了单一刚玉型结构.随V5+针含量的增加,样品的介电常数ε和品质因数Q·f先增大后减小,样品的谐振频率温度系数Tf逐渐减小,这是由于V5+的取代使得B位键价增强所致.在x=0.15,1250℃烧结,可获得εr=9.98,Q·f=20248GHz(8GHz),Tf=-23.3x10-6.K-1的新型微波介质陶瓷.
参考文献
| [1] | Li Y,Chen X M.J.Euro.Ceram.Soc.,2002,22(5):715-719. |
| [2] | Kim W S,Kim E S,Yoon K H.J.Am.Ceram.Soc.,1999,82(8):2111-2115. |
| [3] | 吕文中,朱建华,Kipkoech E R(LU Wen-Zhong,et al.无机材料学报(Journal of Inorganic Materials),2006,21(1):139-144. |
| [4] | 赵梅瑜,王依琳.电子元件与材料,2005,24(12):50-54. |
| [5] | Kumada N,Taki K,Kinomura N.Mater.Res.Bull.,2000,35(7):1017-1021. |
| [6] | Yokoi A,Ogawa H,Kan A.J.Ceram.Soc.Jpn,2004,112:S1633-S1636(Supplement 112-1 PacRim 5 Special Issue). |
| [7] | Liu P,Yao G G,Bian X B,et al.J.Electroceram.,In press.(DOI:10.1007/s10832-007-9114-6). |
| [8] | Lim S W,Bang J.J.Electroceram.,In press(DOI:10.1007/s10832-007-9322-0). |
| [9] | Hirotaka Ogawa,Akinori Kan,Soichi Ishihara.J.Euro.Ceram.Soc.,2003,23(14):2485-2488. |
| [10] | Kan A,Ogawa H.Mater.Res.Bull.,2006,44(6):1178-1184. |
| [11] | Yoshida A,Ogawa H,Kan A.J.Euro.Ceram.Soc.,2004,24(6):1765-1768. |
| [12] | Ogawa H,Taketani H,Kan A.J.Euro.Ceram.Soc.,2005,25(12):2859-2863. |
| [13] | Kan A,Ogawa H.Jpn.J.Appl.Phys.,2003,42(9B):6154-6157. |
| [14] | Fan X C,Chen X M.IEEE Trans.Microwave Theor.Tech,2005,53:3130-3134. |
| [15] | 吕孟凯.固态化学.济南:山东大学出版社.183-185. |
| [16] | Bosman A J,Havinga E E.Phys.Rev.,1963,129(4):1593-1600. |
| [17] | Wee S H,Kim D W,Yoon S I.J.Am.Ceram.Soc.,2004,87(5):871-874. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%