采用溶胶-凝胶法制备硅铝二元膜包覆稀土发光材料.通过扫描电镜、X光电子能谱、比表面、多晶X射线衍射、荧光光谱和发光亮度的测试,研究了材料的结构、包覆层与原始发光材料的相互作用及材料发光性能;进一步通过pH值测定,考察了材料的耐水性.结果表明,包覆层以无定型态与原始发光材料以化学作用结合,而不是简单的物理包覆;在原始发光材料表面包覆一层均匀的硅铝二元膜,可有效提高材料的耐水性能,而对材料的发光性能影响不大.
参考文献
| [1] | Picht,Friederike,Merikhi,et al.Phosphor composition comprising fine-grain and coarse-grain SiO2 particles.United States Patent,No.6,010,779,2000-1-4. |
| [2] | Picht,Friederike,Bredol,et al.Phosphor composition with a coating of colloidal SiO2 particles and an oxygen compound of magnesium,calcium,barium,zinc or aluminum.United States Patent,No.6,013,979,2000-1-11. |
| [3] | 崔洪涛,张耀文,洪广言.功能材料,2001,32(6):564-569. |
| [4] | ZHANG Jun-ying,CHEN Qing-ming,LIN Yuan-hua,et al.Rear Metals,2002,21 (2):152-155. |
| [5] | 周文华,刘又年,吕兴栋,等.广州化工,2004,32(4):31-33. |
| [6] | 吕兴栋,舒万艮,谭爱东,等.(LU Xing-Dong,et al).无机材料学报(Journal of Inorganic Materials),2004,19(6):1373-1378. |
| [7] | 罗昔贤,郑笑全,段锦霞,等(LUO Xi-Xian,et al).硅酸盐学报(Journal of the Chinese Ceramic Society),2003,31(11):1058-1062. |
| [8] | Kozuka,Ko,Kobayashi,et al.Polymerizable emulsifying agent and application thereof.United States Patent.No.3,980,622,1976-9-14. |
| [9] | Goebel K H,Stahler K,von Berlepsch H.Colloids and Surfaces A:1994,87:143-149. |
| [10] | 李强,高濂,严东生(LI Qiang,et al).无机材料学报(Journal of Inorganic Materials),1999,14 (1):150-154. |
| [11] | 熊蓉春,曹朋,王连盛,等.北京化工大学学报,2005,32(3):61-65. |
| [12] | 曹福想,严坤,张科元.南方金属,2005,144:20-23. |
| [13] | 李大东,钟孝湘编译.催化剂载体与负载型催化剂,第一版.北京:中国石化出版社,1992.15-24. |
| [14] | 熊煜虹,王东,陆毅青,等(XIONG Yu-Hong,et al).无机材料学报(Journal of Inorganic Materials),2003,18(2):451-456. |
| [15] | 肖志国,罗昔贤.蓄光型发光材料及其制品,第二版.北京:化学工业出版社,2005.177. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%