以钛酸正丁酯为前驱体,乙酰丙酮为络合剂,分别在室温和70℃进行对前驱体改性的络合反应,获得改性前驱体Ti(O-Bu)4-x(AcAc)x.以异丙醇为溶剂,采用溶胶-凝胶(sol-gel)法制备0.1～3.0mol%Er3+掺杂TiO2粉末.差热-热重(TG-DTA)分析结果表明,由室温络合改性前驱体制备的粉末,无定型到锐钛矿和锐钛矿到金红石的相变温度,较由70℃络合改性前驱体制备的粉末均升高40℃.X射线衍射(XRD)分析表明,700℃烧结,室温络合所得掺0.1～3.0mol%Er3+:TiO2粉末为单一锐钛矿结构,70℃络合所得粉末为锐钛矿和少量金红石的混合相结构.400～800℃烧结,两种络合所得粉末均获得中心波长为1.53μm的多峰结构光致发光(PL)谱.其中,700℃烧结的粉末PL强度最强.70℃络合较室温络合的粉末PL强度可提高3倍.
参考文献
| [1] | Guo H,Zhang W,Lou L,et al.Thin Solid Films,2004,458:274-280. |
| [2] | Nekvindov P,Cerven J,Capek P,et al.Opt.Mater,2003,24:527-535. |
| [3] | Wang X J,Lei M K.Thin Solid Films,2005,476:41-45. |
| [4] | 杨涛,王兴军,王辉,等(YANG Tao,et al).无机材料学报(Journal of Inorganic Materials),2004,19(3):671-674. |
| [5] | Strohhofer C,Polman A.Opt.Mater,2003,21:705-712. |
| [6] | Chen S Y,Ting Ch Ch.Thin Solid Films,2003,434:171-177. |
| [7] | 杜宏伟,孔瑛.应用化学,2002,19(9):882-885. |
| [8] | Bahtat A,Bouazaoui M,Bahtat M,et al.J.Non-Crys Solids,1996,202:16-22. |
| [9] | Djaoued Y,Ta R,Bruning R,et al.J.Non-Crys Solids,2002,297 (1):55-66. |
| [10] | 温敏,齐公台,孙菊梅.表面技术,2004,33(1):30-32. |
| [11] | 程银兵,马建华,吴广明,等.功能材料,2003,34(1):73-75. |
| [12] | Bahtat A,Bouazaoui M,Bahtat M.Opt.Comm,1994,111:55-60. |
| [13] | 王永为,吴凤清,阮圣平,等.功能材料,2003,34(1):93-95. |
| [14] | Suresh C,Mukundan P,et al.Polyhedron,1998,17 (18):3131-3135. |
| [15] | Zhang Q H,Gao L,Guo J K.J.Appl.Catal.B,2000,26:207-215. |
| [16] | Isshiki H,Polman A,Kimura T.J.Luminescence,2003,102-103:819-824. |
| [17] | Orazio A D,Sario M De,Mescia L V,et al.J.Non-Crys Solids,2003,322 (3):278-283. |
| [18] | Block B A,Wessels B W.Appl.Phys.Lett.,1994,65 (1):25-27. |
| [19] | Judd B R.Phys.Rev.,1962,127 (3):750-761. |
| [20] | Moon R M,Koehler W C,Child H R,et al.Phys.Rev.,1968,176 (2):176-185. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%