以硝酸镁、硼酸、柠檬酸为原料,利用溶胶-凝胶法及不同温度后续煅烧制备了硼酸镁(MgB4O7和Mg2B2O5)纳米棒.用X射线衍射(XRD)分析了纳米棒的结构,用扫描电子显微镜(SEM)和透射电子显微镜(TEM)观察了纳米棒的形貌.实验结果表明,750℃煅烧产物为MgB4O7纳米棒,950℃煅烧产物为Mg2B2O5纳米棒,纳米棒的径长比可以通过调节原料硝酸镁和硼酸的比例来控制.用自催化机理解释了硼酸镁纳米棒的生长机理.
参考文献
| [1] | Gudiksen M S,Lauhon L J,Wang J,et al.Nature,2002,415:617-620. |
| [2] | Calvert P.Nature,1999,399:210-211. |
| [3] | Sha J,Niu J,Ma X,et al.Adv.Mater.,2002,14:1219-1221. |
| [4] | Yang Q,Sha J,Xu J,et al.Chem.Phys.Lett.,2003,379:87-90. |
| [5] | Yang Q,Sha J,Ma X,et al.Supercond Sci.Technol.,2004,17:31-33. |
| [6] | Yang Q,Sha J,Wang L,et al.Physica E,2005,27:319-324. |
| [7] | Peng L M,Zhu S J,Ma Z Y.Mater.Sci.Eng.A,1999,265:63-70. |
| [8] | Furetta C,Prokic M,Salamon R,et al.Appl.Radiation and Isotopes,2000,52:243-250. |
| [9] | LIU Y,LI Q,FAN S.Chem.Phys.Lett.,2003,375:632-635. |
| [10] | Cheng C,Tang C,Ding X X,et al.Chem.Phys.Lett.,2003,373:626-629. |
| [11] | Ma R,Bando Y,Sato T.App.Phys.Lett.,2002,81(18):3467-3469. |
| [12] | Ma R,Bando Y,Sato T,et al.J.Am.Chem.Soc.,2002,124:10668-10669. |
| [13] | Ma R,Bando Y,Golberg D,et al.Angew.Chem.Int.Ed,2003,42:1836-1838. |
| [14] | Qasrawi A F,Kayed T S,Mergen A,et al.Mater.Res.Bull.,2005,40:583-589. |
| [15] | Yang Q,Sha J,Ma X,et al.Materials Letters,2005,59:1967-1970. |
| [16] | 李昱,张孝彬,徐军明,等(LI Yu,et al).无机材料学报(Journal of Inorganic Materials),2005,20(1):71-76. |
| [17] | 张巍巍,谢平波,张慰萍,等(ZHANG Wei-Wei,et al).无机材料学报(Journal of Inorganic Materials),2001,16(1):10-15. |
| [18] | Wanger R S,Ellis W C.Appl.Phys.Lett.,1964,4(5):89-90. |
| [19] | Duan X F,Wang J F,Lieber C M.Appl.Phys.Lett.,2000,76(9):1116-1118. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%