提出了一种合成孔壁含有沸石结构单元的介孔结构材料的新方法-降解法,即利用不同硅铝比的β沸石和ZSM-5沸石为原料在碱溶液中处理得到降解液,然后以此降解液为硅铝源在表面活性剂P123的模板作用下组装了孔结构类型为SBA-15的介孔结构材料,分别简称为MSB(β沸石降解合成)和MSZ(ZSM-5沸石降解合成).产物的IR光谱、N2吸附、29Si MAS NMR图谱和对重芳烃的加氢脱烷基反应催化活性均说明降解法合成的介孔结构材料MSB和MSZ的孔壁中含有了沸石的结构单元.
参考文献
| [1] | Davis M. Nature, 2002, 417: 813-828. |
| [2] | Kloetstra K R, Zandbergen H W, Jansen J C. Micropor. Mater., 1996, (6): 287-293. |
| [3] | Karlsson A, Stocker M, Schmidt R. Micropor. Mesopor. Mater., 1999, (27): 181-192. |
| [4] | Poladi RH P R, Christopher C L. Micropor. Mesopor. Mater., 2002, (52): 11-18. |
| [5] | Prokesova P, Mintova S, Cejka J, et al. Micropor. Mesopor. Mater., 2003, (64): 165-174. |
| [6] | Kloetstra K R, Zandbergen H W, Jansen J C. Micropor. Mater., 1996, (6): 287-293. |
| [7] | Kloetdtra K R, Bekkum H V, Jansen C. Chem. Commun., 1997. 2281-2282. |
| [8] | Trong On Do, Kaliaguine S. Angew. Chem. Int. Ed, 2001, 17: 40. |
| [9] | Huang L M, Guo W, Deng P. J. Phys. Chem. B, 2000, 104: 2817-2823. |
| [10] | Liu Y, Zhang W, Pinnavaia T J. Angew. Chem. Int. Ed., 2001, 40: 1255. |
| [11] | Zhang Z, Han Y, Zhu L, et al. Angew. Chem. Int. Ed., 2001, 40: 1258. |
| [12] | Zhang Z T, Han Y, Xiao F S, et al. J. Am. Chem. Soc., 2001, 123: 5014-5021. |
| [13] | Han Y, Wu S, Sun Y, et al. Chem. Mater., 2002, 14: 1144. |
| [14] | 谢在库, 陈庆龄, 张成芳. 石油化工, 1999, 28 (6): 408-413. |
| [15] | Cizmek A, Subotic B, Aiello R, et al. Micropor. Mater, 1995, (4): 159-168. |
| [16] | Lechert H, Kacirek H. Zeolites, 1991, (11): 720-725. |
| [17] | Dessau R M, Valyocsik E W, Goeke N H. Zeolites, 1992, (12): 776. |
| [18] | Ogura M, Shinomiya S, Tateno J, et al. Appl Catal A, 2001, 219: 33-43. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%