分析了掺Er3+碲酸盐玻璃的热力学稳定性能,研究了掺Er3+碲酸盐玻璃的吸收和荧光光谱性质;应用Judd-Ofelt理论计算了碲酸盐玻璃中Er3+离子的强度参数Ω(Ω2=4.79×10-20cm2,Ω4=1.52×10-20cm2,Ω6=0.66×10-20cm2),计算了离子的自发跃迁几率,荧光分支比;应用Mc-Cumber理论计算了Er3+的受激发射截面(σe=10 40×10-21cm2)、Er3+离子4I13/2→4I15/2发射谱的荧光半高宽(FWHM=65.5nm)及各能级的荧光寿命(4I13/2能级为Trad=3.99ms);比较了不同基质玻璃中Er3+离子的光谱特性,结果表明掺铒碲酸盐玻璃更适合于掺Er3+光纤放大器实现宽带和高增益放大.
参考文献
| [1] | Masuda H, Kawai S, Aida K. Electronic letters, 1998, 34 (13): 1342-1343. |
| [2] | Jiang S, Luo T, Hwang B C, et al. Non-Cryst. Solids, 2000, 263: 364-368. |
| [3] | Hwang B C, Jiang S B, Luo T, et al. IEEE Photo. Tech. Lett., 2001, 13 (3): 197-199. |
| [4] | Tanabe S, Yoshii S, Hirao K, et al. Phys. Rev. B., 1992, 45: 4620-4625. |
| [5] | Feng Y, Hao Z, Chen X B, et al. Acta. Phys. Sin., 1997, 46: 2454-2460. |
| [6] | Wang J S, Vogel E M, Snitzer E. Optical Materials. 1994, 3: 187-192. |
| [7] | Feng X, Tanada T. Am. Ceram. Soc., 2001, 84: 165-171. |
| [8] | Mori A, Kobayashi K, Yamada M. Electron Lett., 1998, 34: 887-893. |
| [9] | Tanabe S, Sugimoto N, Ito S, et al. Non-Cryst. Solids, 2000, 87: 670-675 |
| [10] | Kuroiwa Y, Sugimoto N, Ochiai K, et al. OFC, 2001, Tu15-1. |
| [11] | Choi Y G, Kim K H, Heo J. Am. Ceram. Soc., 1999, 82: 2762-2768. |
| [12] | Wang J S, Vogel E M, Snitzer E. Optical Materials, 1994, (3): 187-203. |
| [13] | Wang J S, Vogel E M, Snitzer E, et al. Non-Cryst Solids, 1994, 178: 109. |
| [14] | Judd B R. Phys. Rev., 1962, 127 (3): 750-761. |
| [15] | Ofelt G S. J. Chem. Phys., 1962, 37 (3): 511-520. |
| [16] | Tanabe S. Non-Cryst Solids, 1999, 259: 1-6. |
| [17] | Zou X, Izumitani T. Non-Cryst. Solids, 1993, 162: 68-72. |
| [18] | McCumber D E. Phys. Rev., 1964, 134 (2A): A299-A306. |
| [19] | Lin H, Pun E Y B, Man S Q, et al. Opt. Soc. Am. B., 2001, 18: 602-605. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%