以单齿络合剂甲胺为辅助通过水热法制备了CdS纳米棒,所得CdS纳米棒分别用TEM、XRD、Raman和PL等技术进行了表征.研究了络合剂甲胺的浓度对CdS纳米晶体形貌的影响.实验发现当络合剂甲胺的浓度为1、5和20wt%时,水热合成CdS纳米晶体的形貌分别为纳米颗粒、短纳米棒和长纳米棒.这也表明络合剂的类型即单齿或双齿络合剂并不是水热合成CdS纳米棒形成的关键因素.基于实验结果,提出了一个可能的水热合成CdS纳米棒的形成机制:络合物结构-控制机理.
参考文献
| [1] | Dai H, Wong E W, Lieber C M, et al. Nature, 1995, 375: 769-772. |
| [2] | Yang P D, Lieber C M. Science, 1996, 273: 1836-1840. |
| [3] | Braun E, Eichen Y, Sivan U, et al. Nature, 1998, 391: 775-778. |
| [4] | Yan P, Xie Y, Qian Y T, et al. Chem. Commun., 1999. 1293-1294. |
| [5] | Brus L E. Appl. Phys. A, 1991, 53: 465-468. |
| [6] | Kolmakov K Y, Pak V N, Russ J. App. Chem., 1999, 72: 1192-1195. |
| [7] | Vaslltsova O V, Parmon V N. Kinetics and Catalysis, 1999, 40: 62-65. |
| [8] | Heske C, Winkler U, Neureiter H, et al. Appl. Phys. Lett., 1997, 70: 1022-1024. |
| [9] | Cao H Q, Hu Y, Hong J M, et al. Adv. Mater., 2001, 13: 1393-1394. |
| [10] | Routkevitch D, Bigioni T, Moskovits M, et al. J. Phys. Chem., 1996, 100: 14037-14047. |
| [11] | Jun Y W, Lee S M, Kang N J, et al. J. Am. Chem. Soc., 2001, 123: 5150-5151. |
| [12] | Ge X W, Ni Y H, Zhang Z C. Radiation Physics and Chemistry, 2002, 64: 223-227. |
| [13] | Li Y D, Liao H W, Ding Y, et al. Inorg. Chem., 1999, 38: 1382-1387. |
| [14] | Yang J, Zeng J H, Yu S H, et al. Chem. Mater., 2000, 12: 3259-3263. |
| [15] | Arguello C A, Rousseau D L, Porto S P S. Phys. Rev., 1969, 181: 1351-1355. |
| [16] | Nanda K K, Sahu S N. Solid State Comm., 1999, 111: 671-675. |
| [17] | Li Y D, Sui M, Ding Y, et al. Adv. Mater., 2000, 12: 818-821. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%