采用sol-gel法和机械化学法相结合制备了改性高岭土/钛氧化物颗粒,与甲基硅油配制成电流变液.XRD、FTIR分析表明,钛氧化物以含介孔的非晶态形式包覆在经过机械化学法制备的高岭土/NaCl复合物上,形成改性高岭土/钛氧化物复合颗粒.电流变性能测试表明,当颗粒体积分数为25%,E=3 kV/mm时,复合颗粒电流变液的静态屈服应力达7 kPa,是高岭土电流变液的9倍.同时发现钛氧化物含量对电流变效应有重要影响.电流变液介电性能的变化是其流变学性能提高的起源.
参考文献
| [1] | Block H, Kelly J P. J. Phys. D: Appl. Phys., 1988, 21: 1661-1677. |
| [2] | Halsay T C. Science, 1992, 258: 761-766. |
| [3] | Davis L C. J. Appl. Phys., 1992, 72: 1334-1345. |
| [4] | 尹剑波,赵晓鹏.材料导报,2000,14(9):10-13. |
| [5] | Yin J B, Zhao X P. J. Phys. D. Appl. Phys., 2001, 12: 2603-2605. |
| [6] | Yin J B, Zhao X P. Chem. Mater., 2002, 14: 4663-4668. |
| [7] | Frost R L, Tran T H, Kristof J. Clay Minerals, 1997, 32: 587-596. |
| [8] | Frost R L., Kristof J, Horvath E, et al. J. Colloid Interface Sci., 1999, 214: 380-388. |
| [9] | Michaelian K H, Lapides I, Lahav N, et al. J. Colloid Interface Sci., 1998, 204: 389-393. |
| [10] | 王宝祥,李佳,赵晓鹏(Wang B X,et al.).化学学报(Acta Chim.Sinica),2003,61(2):240-244. |
| [11] | Wang B X, Zhao X P. J. Mater. Chem., 2002, 12 (6): 1865-1869. |
| [12] | Wang B X, Zhao X P. J. Mater. Chem., 2002, 12 (10): 2869-2871. |
| [13] | 董岩,朱以华,匡继,等(Dong Yang Yan et al.)无机材料学报(Journal of Inorganic Materials),2001,16(5): 839-845. |
| [14] | Zhao X P, Yin J B. Chem. Mater., 2002, 14: 2258-2263. |
| [15] | 赵晓鹏,王宝祥,左朝阳.中国发明专利(03114669.4,2003). |
| [16] | 赵晓鹏,王宝祥,左朝阳.中国发明专利(03114668.6,2003). |
| [17] | Frost R L, Kristof J, Horvath E, et al. J. of Raman Spectroscopy, 2001, 32: 271-277. |
| [18] | Frost R L, Mako E, Kristof J, et al. Langmuir, 2001, 17: 4731. |
| [19] | Cho M S, Choi H J, To K. Macromol. Rapid Commun., 1998, 19: 271-273. |
| [20] | Lu J, Zhao X P. J. Mater. Res., 2002, 17 (6): 1513-1519. |
| [21] | Hao T, Kawai A, Ikazaki F. Langmuir, 1999, 15: 921-958. |
| [22] | Block H, Kelly J P, Qin A, et al. Langmuir, 1990, 6: 6-15. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%