以Co0.3Ni0.7(OH)2和LiOH.H2O为原料,在含羟基的有机溶剂水溶液中浸渍呈流变相,用喷雾干燥后于空气中在不同的温度下煅烧16h制备层状LiCo0.3Ni0.7O2正极材料,用XRD、TG-DTA、SEM以及激光粒度测试等表征了材料的晶体结构与理化性能.结果表明,由本法可降低样品合成的反应温度和对反应气氛的严格要求,制备出的样品可有效抑制材料中阳离子混排及非化学计量产物的出现,大大降低材料的首次不可逆放电容量,提高材料的首次放电效率.经700°C煅烧16h合成出的样品首次放电容量达172mAh/g,首次放电效率可达90.8%,循环40次后容量仅衰减9%,显示出优良的电化学性能.
参考文献
| [1] | Johnson C S, Kropf A J. Electrochimica Acta, 2002, 47: 3187-3194. |
| [2] | George Ting-Kuo Fey, Subramanian V, et al. Solid State Ionics, 2002, 152-153: 83-90. |
| [3] | Delmas C. J. Power Source, 1997, 68: 120-125. |
| [4] | Yang H X. J. Power Source, 1999, 79: 261-265. |
| [5] | Julien C, Letraochant C, Rongan S, et al. Materihls Science and Engineerin9. 2000, B76: 145-155. |
| [6] | Rougier A. Solid State Ionics, 1996, 90: 83-90. |
| [7] | Chang C. Solid State Ionics, 1998, 112: 329-344. |
| [8] | Julien C, Michael S S, Zielkienicz S. International Journal of Inorganic Materials, 1999, 29-37. |
| [9] | Subramanian V, George Ting-Kuo Fey. Solid State Ionics, 2002, 148: 351-358. |
| [10] | Kim Woo-Seong, Chung Kwang-il, et al. J. Power Source, 2003, 115: 101-109. |
| [11] | 应皆荣,万春荣,姜长印(YIN Jie-R0ng,et al).无机材料学报(Joumal of Inorganic Materials),2001,16(5):821-826. |
| [12] | Lee Kyung-keun. J. Electrochem. Soc., 2000, 147 (3): 1709-1717. |
| [13] | Kanno R, Kubo H, Kawamoto Y, et al. J. Solid State Chem., 1994, 10: 216-221. |
| [14] | Peres J P, Delmas C, et al. J. Electrochem. Solid, 1996, 57 (6-8): 1057-1060. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%