采用电沉积方法直接在铜集流体上沉积一层可与锂反应的活性金属锡,在氩气气氛中烧结处理后作为锂离子电池的负极.扫描电镜和X射线衍射分析及模拟电池的电化学性能测试结果表明:电沉积工艺制备的锡电极与传统的涂浆法制备的锡电极相比,其首次循环的放电比容量有很大提高,即由442mAh.g-1提高到747mAh·g-1;烧结处理前后电极表面结构、组成和粒度大小不同,锡晶粒粒度分别为102.4、121.0nm;烧结处理后,虽然首次循环的比容量下降为409mAh·g-1,但库仑效率有很大提高,达到92%,30次循环的容量保持率达到58%.
参考文献
| [1] | Kuribyashi I, Yokoyama M, Yamashita M. J. Power Sources, 1995, 54: 1-5. |
| [2] | Ein-Eli Y, Koch V R. J. Electrochem. Soc., 1997, 144 (9): 2968-2973. |
| [3] | Menchem C M, Peled E, Burstein L, et al. J. Power. Sources, 1997, 68: 227-282. |
| [4] | Tsuyoshi N, Katsuouori Y. Denki Kagaku, 1996, 64: 922-923. |
| [5] | Okuno G, Kodayokawa K, Sato Y. Denki Kagaku, 1997, 65 (3): 296. |
| [6] | Mabuchi A, Tokimitsu K, Fjuimoto H, et al. J. Electrochem. Soc., 1995, 142 (4): 1041. |
| [7] | Bensenhard J O, Yang J, Winter M. J. Power Sources, 1997, 68: 87. |
| [8] | Yang J, Wachtler M, Winter M, et al. Electrochem. Solid-State Lett., 1999, 2: 161. |
| [9] | Ehrlich G M, Durand C, Chen X, et al. J. Electrochem. Soc., 2000, 147: 886. |
| [10] | Yang J, Takeda Y, Imanishi N, et al. J. Power Sources, 1999, 79: 220. |
| [11] | Kim Hanusu, Choi Junghee, Sohn Hun-Joon, et al. J Electrochem Soc., 1999, 146 (12): 4401-4405. |
| [12] | Machill S, Rahner D. J Power Sources, 1997, 68: 506-509. |
| [13] | Wachtler Mario, Winter Martin, Besenhard Jurgen O. J. Power Sources, 2002, 15: 49-58. |
| [14] | Winter M, Besenhard J O. Electrochimica Acta, 1999, 45: 31-50. |
| [15] | Larcher D, Beaulieu L Y, MacNeil D D, et al. J. Electrochem. Soc., 2000, 147: 1658-1662. |
| [16] | Yongyao Xia, Tetsuo Sakai, et al. J. Electrochemical Society, 2001, 148 (5): A471-A481. |
| [17] | Noriyuki Tamura, Ryuji Ohshita, Masahisa Fujimoto, et al. J. Power Sources, 2002, 107: 48-55. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%