用传统固相法成功制备出了致密的、相对密度超过95%的Bi3NbTiO9(BNT)压电陶瓷;采用XRD和SEM对陶瓷的结构和晶粒形貌进行了表征;测出了BNT陶瓷在居里温度点附近的介电特性,同时确定了该陶瓷的居里温度Tc为914℃.电滞回线的测试显示了该材料典型的硬铁电性,经过高温极化,测出材料的压电常数d33=7 pC/N.
参考文献
[1] | Smolenskii G A, Isupov A V, Agranovskaya A I. Fiz. Tverd. Tela, 1959, 1: 169-173. |
[2] | Subbarao E C. Phys. Rev., 1961, 122 (3): 804-807. |
[3] | Subbarao E C. J. Phys. & Chem. Solids, 1962, 23: 665-676. |
[4] | Newnham R E, Wolfe R W, Dorrian J F. Mater. Res. Bull., 1971, 6: 1029-1039. |
[5] | Tadashi Takenaka, Koiohiro sakata. J. Appl. Phys, 1984, 55 (4): 1092-1099. |
[6] | Holmes Michael, Newnham Robert E, Cross Leslie E. American Ceramic Society Bulletin, 1979, 58:872. |
[7] | Lin Sheng-He, Swartz S L, Schulze W A, et al. J. Am. Ceram. Soc., 1983, 66: 881-884. |
[8] | Wolfe R W, NEWNHAM R E, SMITH D K. Ferroelectrics, 1971, 3: 1-7. |
[9] | Turer R C, Fuierer P A, Newnham R E, et al. Applied Acoustics, 1994, 41: 299-324. |
[10] | Hellwege K H, Hellwege A M. LANDOLT-BORNSTEIN Ⅲ/16 a: 229-243. |
[11] | Ricote J, Pardo L, Moure A, et al. Journal of the European Ceramic Society, 2001, 21: 1403-1407. |
[12] | A. Lisinska-Czekaj, Czekaj D, Gomes M J M, et al. Journal of the European Ceramic Society, 1999,19: 969-972. |
[13] | Huang Z Z, Chan H L W, KWok K W, et al. J. Mater. Sci, 2000, 35: 1793-1797. |
[14] | Shimakawa Y, Kubo Y, Nakagawa Y, et al. APL, 1999, 74 (13): 1904-1906. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%