用低频扭摆法在多功能内耗仪上测量了巨磁电阻材料La0.7Pb0.3MnO3(LPMO)的温度内耗谱和弹性模量.结果表明,内耗峰位与测量频率无关,并且峰高与频率成反比,弹性模量在对应的内耗峰处有明显的转折,内耗峰表现为相变峰的特征.结合电阻和磁化率的测试,解释了内耗和电阻-温度曲线的双峰现象,高温内耗峰和高温电阻峰与居里温度有很好的对应,来源于顺磁半导体向铁磁金属的转变,低温内耗峰和磁化率的单调下降来源于铁磁相分离过程,而较大的低温电阻峰部分来源于相分离过程.
参考文献
| [1] | Jonker G H, et al. Physica, 1950, 16: 564-573. |
| [2] | Baibich M N, et al. Phys. Rve. Let.t, 1998, 61: 2472-2475. |
| [3] | Helmol t R von, et al. Phys. Rev. Lett., 1993, 71: 2331-2333. |
| [4] | Jin S, et al. Science, 1994, 264 (15): 413-415. |
| [5] | Xiong G C, et al. Appl. Phys. Lett., 1995, 66 (11): 1427-1429. |
| [6] | Liu K, et al. Phys. Rev. B., 1996, 54: 3007-3010. |
| [7] | Zhang N, et al. Solid State Commun., 1988, 107 (8): 417-422. |
| [8] | @@Staduik Z M,@@ et al.$$ Phys. Rev. B,** 1987,)) 35:&& 6588-6592; |
| [9] | @@Sattler K,@@ et al.$$ Phys. Rev. Lett.,** 1980,)) 45:&&821-824 |
| [10] | Cowen J A, et al. J. Appl. Phys., 1987, 61: 3317-3319. |
| [11] | Zheng LQ, Fang Q F. J. Phys. :Condensed Matt., 2001, 13: 3411-3418. |
| [12] | Li H Q, et al. Scripta Materialia, 2002, 46: 691-694. |
| [13] | Hueso L E, et al. J. Appl. Phys., 1999, 86: 3881-3884. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%