采用溶胶-凝胶法制备了掺杂不同浓度Sm2O3(分别为0.001,0.002,0.003,0.005,0.007mol)的BaTiO3陶瓷,并对其结构与电性能进行了研究.结果表明:Sm2O3掺杂BaTiO3陶瓷的晶型在室温下为四方相,而且随着Sm2O3掺杂浓度的增加,BaTiO3陶瓷的晶粒尺寸变小,说明Sm2O3掺杂对BaTiO3陶瓷晶粒的生长有一定的抑制作用;Sm2O3掺杂BaTiO3陶瓷的电阻率比纯BaTiO3陶瓷明显下降,当添加量为0.001mol时,电阻率最小,.从4.3×109Ω@m下降为6.536×103Ω@m;Sm2O3掺杂BaTiO3陶瓷的晶粒电阻随着温度的变化,呈现NTC效应,而晶界电阻随着温度的变化,呈现PTC效应,且晶界电阻远远大于晶粒电阻,说明该材料的PTC效应是由晶界效应引起的.
参考文献
| [1] | Nosaka Y, Jimbo M, Aizawa M. Journal of Materials Science Letters, 1991, 10: 406-407. |
| [2] | Kowalski K, Ijjaali M, Bak T, et al. J. Phy. Chem. of Solids, 2001, 62: 543-551. |
| [3] | Yamaji A, Enomoto Y, Kinoshita K. J. Am. Ceram. Soc., 1977, 60 (3): 97-101. |
| [4] | Shaikh A, Robert W V. J. Am. Ceram. Soc., 1986, 69 (9): 689-694. |
| [5] | 郝素娥,韦永德,韦华(HAO Su-E,et al).无机化学学报(Journal ofInorganic Materials),2002,18(6):623-625. |
| [6] | Shimooka H,Makoto K.J.Am.Ceram.Soc.,1995,78(10):2849-2852. |
| [7] | 唐小锋,唐子龙,周志刚(YANG Xiao-Feng,et al).无机材料学报(Journal of Inorganic Materials),2000,15(6):1037-1042. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%