以沉淀法制备的纳米Cr2O3为原料,采用氨解法在800～900℃、氮化4～8h制备了纳米氮化铬粉体.对不同氨解温度、氨解时间合成的CrN粉体用X射线衍射(XRD)、透射电镜(TEM)等方法进行了表征.研究了氨解温度、氨解时间对CrN粉体性能的影响.结果表明:该方法所需设备简单,氮化温度低,反应时间短,产品纯度高.在800℃氮化8h可得到粒度为40～80nm的纯立方相CrN纳米粉体.
参考文献
| [1] | Disalvo F J. Science, 1990, 247: 649-655. |
| [2] | Volpe L, Boudart M J. Solid State Chem., 1985, 59:332-347 |
| [3] | Navinsek B, Panjan P, Cvelbar A. Surf. Coat. Tecknol., 1995, 74/75(1-3): 155-161. |
| [4] | Herr W, Mattes B, Broxzeit E, et al. Surf. Coat. Technol., 1993, 60(1-3): 428-433. |
| [5] | Lai F D, Wu J K. Surf. Coat. Technol., 1996, 88(1-3): 183-189. |
| [6] | Qian X F, Zhang X M, Wang C, et al. Mater. Res. Bull., 1999, 34: 433-436. |
| [7] | Ren R M, Yang Z G, Shaw Leon L. Nanastruct Mater., 1999, 11(1): 25-35. |
| [8] | Calka A, Williams J S. Mater Sci. Forum., 1992, 88-90: 787-794. |
| [9] | Yoshihiko Takano, Masahiro Hachiya, Masaru Yoshinaka, et al. J. Am. Ceram. Soc., 2000, 83(2):448-450. |
| [10] | Roger Marchand, Yves Laurent, Jean Guyader, et al. J. Eur. Ceram. Soc., 1991, 8: 197-213. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%