研究了β-Al2O3粉体材料的制备工艺与性质，这种粉体材料可以采用慢速升温、分阶段保温的工艺，煅烧Li2CO3、Na2CO3和Al2O3的均匀混合物不经球磨直接制得.根据使用要求与生产条件，混合物可用干混、半湿混-过筛或喷雾干燥法来制备.粉体材料主要由β/β"-Al2O3组成，β"相的相对含量>70%，加入适当的粘结剂与溶剂,可将其制成大气环境中金属管道外的固体电解质涂层.涂层中粉体的化学与电化学性能稳定，其阴极极化曲线有明显的平坦区，可用于阴极保护技术.
-Al2O3 powdered material could be prepared from the mixtures of Li2CO3, Na2CO3 and Al2O3, which were obtained by dry mixing, wet mix-screening or spray-drying process, by stepped calculating without grinding. The effect of preparation condition on the properties of the powdered material was showed. The powder composed of /′′-Al2O3 in principle, f(′′)>70%, could be fabricated into solid electrolytic coating for metal pipeline in atmosphere, with some binders and solvents.The powder in the coating was stable chemically and electrochemically to metal, binders and moistur. The polarization behavior of cathode for “Beta-coating” showed that there was a flat at the polarization curve, which could be evaluated for the cathode protection of metal in atmosphere.
参考文献
| [1] | 华东输油管理局. “气相环境中金属管道阴极保护技术”说明书. 1987. |
| [2] | Weber N, Kummer J T. Proc. 21st Annual Power Sources Conf. 1967. 21, 42. |
| [3] | Chen K G, Lin Z X, Fan Z Z. Proc.: DOE/EPRI (Sodium-sulfur) Battery Workshop V Dec. 1984. 6: 237--250. |
| [4] | Youngblood G, Virkar A, Cannon W R, et al. Amer. Ceram. Bull., 1977, 56 (2): 206--210, 212. |
| [5] | 陈昆刚,林祖纕,徐孝和. 硅酸盐学报, 1986, 14 (2): 171--174. |
| [6] | 陈昆刚, 林祖纕, 杨淑平, 等. 硅酸盐学报, 1984, 12 (4): 445--449. |
| [7] | 林祖, 郭祝昆, 等. 快离子导体. 上海: 上海科技出版社, 1983. 153, 219 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%