本文运用嵌入原子簇的电荷自洽离散变分方法(SCC-DVM-Xα方法)分别对TiO2晶体中F和F+心的能级结构进行了计算,得到了F和F+心的光学吸收跃迁模式,其跃迁能量分别是0.98、1.78eV.我们认为,经还原后的TiO2晶体,在光吸收实验中测到的1.2μm(1.02eV)、760nm(1.75eV)两个峰分别是由于还原过程中形成的F和F+心的吸收峰, 并存在着F→F+的转型过程.
参考文献
| [1] | Hasiguti Ryukiti R, Yagi Eiichi. Phys. Rew. B, 1994, 15: 7251-7256 |
| [2] | Breckenridge Robert G, Hosler William R. Phys. Rev, 1953, 91: 793-802 |
| [3] | Halley J W, Michalewicz M T, Tit N. Phys. Rew. B, 1990, 41: 10165-10170 |
| [4] | Aono M, Hasguti R P. Phy. Rev. B, 1993, 48: 12406-12414 |
| [5] | Cronemeyer D C. Phys. Rev. 1952, 87: 876-886 |
| [6] | Cronemeyer D C. Phys. Rev. 1959, 113: 1222-1226 |
| [7] | Stashans A, Lunell S, Grimes R W. J. Phys. Chem. Solids, 1995, 57: 1293-1301 |
| [8] | Henrich Victor E, Dresselhaus G, Zeiger H J. Phys. Rev. Lett., 1976, 36: 1335-1339 |
| [9] | 卢铁城. 博士学位论文,四川联合大学,1997, 9: 5-339 |
| [10] | Lin Li-Bin, Mo Shang-di, et al. J. Phys. Chem. Solids, 1993, 54 (8): 907-912 |
| [11] | Mo Shang-di, Lin Li-Bin, et al. J. Phys. Chem. Solids, 1994, 55 (11): 1309-1313 |
| [12] | |
| [13] | 方书鑫, 张启仁. 晶体色心物理学. 上海: 上海交通大学出版社,1989. 61-64 |
| [14] | Ferrari A M,Pacchioni G. J. Phys. Chem., 1995, 99: 17010-17018 |
| [15] | Kowalczyk S P, et al. Solid State Comm, 1977, 23: 161-170 |
| [16] | Tossell J A, et al. Am. Mineral, 1974, 59: 319-325 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%