利用电化学、金相、能谱等方法,研究了低碳贝氏体钢在表面锈层受到不同程度的损伤后,在含Cl-环境中的继续腐蚀行为.实验发现,低碳贝氏体钢和作为对比材料的低碳钢试样的表面锈层受损伤后,在继续腐蚀过程中均能很快得到修复.在损伤程度与继续腐蚀时间相同的条件下,低碳贝氏体钢的锈层电阻与损伤修复率均高于低碳钢.低碳贝氏体钢基体/锈层界面的断裂韧性高于锈层本身.在受外界作用时,锈层不会沿基体/锈层界面彻底脱落从而在基体表面保存残留锈层.残留锈层能明显促进新锈层在损伤部位的形成.原有锈层与损伤部位新形成的锈层中Cu和Cr含量接近,并与钢基体的含量相当.
参考文献
| [1] | Zhao Z Y.The Design of Alloy Steels.Beijing:National Defense Industry Press,1999:106(赵振业.合金钢设计.北京:国防工业出版社,1999:106) |
| [2] | Wang X M,Shang C J,Yang S W,He X L.Acta Metall Sin,2002; 38:661(王学敏,尚成嘉,杨善武,贺信莱.金属学报,2002;38:661) |
| [3] | Shang C J,Wang X M,Yang S W,He X L,Wu H B.Acta Metall Sin,2002; 39:1019(尚成嘉,王学敏,杨善武,贺信莱,武会宾.金属学报,2003;39:1019) |
| [4] | Zhang Z G,Gu Z Y,Liao Y G,Guo Q L,Su F T,Chen Y Z.Electrochemistry,2000; 6:473(张志刚,辜志俊,廖永贵,郭琦龙,苏方腾,陈衍珍.电化学,2000;6:473) |
| [5] | Tan Y J,Bailey S,Kinsella B.Corros Sci,1996; 38:1545 |
| [6] | Nishimura T,Kodama T.Corros Sci,2003; 45:1073 |
| [7] | Nishimura T,Tahara A,Kodama T.Mater Trans,2001;42:478 |
| [8] | Lin C,Li X G,Liu X D.J Chin Soc Corros Prot,2005; 25:4(林翠,李晓刚,刘晓东.中国腐蚀与防护学报,2005;25:4) |
| [9] | Wang J H,Wei F I,Chang Y S,Shih H C.Mater Chem Phys,1997; 47:1 |
| [10] | Han W,Wang J,Wang Z Y,Yu G C,Li H X.J Chin Soc Corros Prot,2004; 24:147(韩薇,汪俊,王振尧,于国才,李洪锡.中国腐蚀与防护学报,2004;24:147) |
| [11] | Nishimura T,Katayama H,Noda K,Kodama T.Corrosion,2000; 56:935 |
| [12] | Wang S T,Yang S W,Gao K W,Shen X A,He X L.Acta Metall Sin,2008; 44:1116(王树涛,杨善武,高克玮,沈晓安,贺信莱.金属学报,2008;44:1116) |
| [13] | Liu L H,Qi H B,Lu Y P,Li X G.Corros Sci Technol Prot,2003; 15:86(刘丽宏,齐慧滨,卢燕平,李晓刚.腐蚀科学与防护技术,2003;15:86) |
| [14] | Choi Y S,Shim J J,Kim J G.J Alloys Compd,2005; 391:162 |
| [15] | Choi Y S,Shim J J,Kim J G.Mater Sci Eng,2004; A385:148 |
| [16] | Zhang Q C,Wang J J,Wu J S,Zheng W L,Chen J G,Li A B.Acta Metall Sin,2001; 37:193(张全成,王建军,吴建生,郑文龙,陈家光,李爱柏.金属学报,2001;37:193) |
| [17] | Matsushima I,Ueno T,Tamada A,Kubota H.Nippon Kokan Technol Rep,1969; 46:249 |
| [18] | Okada H,Hosoi Y,Yukawa K,Naito H.Tetsu-to-Hagané,1969; 55:355(岡田秀弥,细井裙三,汤川悫一,内藤浩光.铁と钢,1969;55:355) |
| [19] | Misawa T,Yamashita M,Matsuda Y,Miyuki H,Nagano H.Tetsu-to-Hagané,1993; 79:69(三沢俊平,山下正人,松田恭司,幸英昭,长野博夫.铁と钢,1993;79:69) |
| [20] | Yamashita M,Miyuki H,Matsuda Y,Nagano H,Misawa T.Corros Sci,1994; 36:283 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%