采用应力松弛实验研究了Zr-4合金的热激活变形与动态应变时效现象.结果表明,合金在应力松弛过程中的塑性变形速率随松弛时间的增加而减小,塑性变形速率和松弛结束时的应力降低比率在623 K附近都会出现最小值.对位错运动的激活体积分析发现,锫合金中位错运动的速率控制机制是位错克服溶质原子的障碍,动态应变时效会导致位错运动的激活体积增大,623 K附近动态应变时效最为显著,位错密度会对合金的动态应变时效产生影响.
参考文献
| [1] | Lee M H,Kim J H,Choi B K,Jeong Y H.J Alloys Compd,2007; 428:99 |
| [2] | Ahn J S,Nam S W.Mater Lett,1990; 9:413 |
| [3] | Lee K W,Kim S K,Kim K T,Hong S I.J Nucl Mater,2001; 295:21 |
| [4] | Thorpe W R,Smith I O.J Nuel Mater,1978; 78:49 |
| [5] | Armas A F,Alvarez I A,Moscato G.Scr Mater,1996; 34:281 |
| [6] | Nemat-Nasser S,Li Y L.Acta Mater,1998; 46:565 |
| [7] | Zhang J S.SSrength of Materials.Harbin:Harbin Institute of Technology Press,2004:52(张俊善.材料强度学.哈尔滨:哈尔滨工业大学出版社,2004:52) |
| [8] | Guo Y B,Tang Z P,Cheng J Y.Acta Mech Solida Sin,2002; 23:249(郭扬波,唐志平,程经毅.固体力学学报,2002;23:249) |
| [9] | Kocks U F,Argon A S,Ashby M F.Prog Mater Sci,1975;19:112 |
| [10] | Regazzoni G,Kocks U F,Follansbee P S.Acta Metall,1987; 35:2865 |
| [11] | Soo P,Higgins G T.Acta Metall,1968; 16:177 |
| [12] | Hong S I,Ryu W S,Rim C S.J Nucl Mater,1984; 120:1 |
| [13] | Schoeck G.Phys Status Solidi,1965; 8:499 |
| [14] | Evans A G,Rawlings R D.Phys Status Solidi,1969; 34:9 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%