采用压力浸渗法制备碳纤维织物(2D Cf)及单向碳纤维(1D Cf)增强镁合金复合材料,测试丁两种复合材料在50-350℃范围内的热膨胀行为.结果表明,2D Cf/镁合金复合材料(简称2D)平面内不同方向的平均热膨胀系数均随温度升高不断降低.从50到350℃,0°/90°方向的甲均热膨胀系数由4.03×10-6℃-1降至1.83×10-6℃-1;45°方向的平均热膨胀系数由4.53×10-6℃-1降至2.31×10-6℃-1.根据推导公式可以准确计算2D增强复合材料20-150℃范围内0°/90°方向的平均热膨胀系数.20～150℃热循环测试结果表明,2D复合材料具有较好的尺寸稳定性,在热循环过程中存在应变滞后现象,其残余塑性变形主要是基体合金在热应力作用下产生的塑性变形,并且从第2次热循环起,复合材料在热循环中产生的净应变不随热循环次数增加而变化.
参考文献
| [1] | Li K,Pei Z L,Gong J,Shi N L,Sun C.Aeta Metall Sin,2007;43:1281(李坤,裴志亮,宫骏,石南林,孙超.金属学报,2007;43:1281) |
| [2] | Goddard D M.Trans Am Foundryrnen's Soc,1986;94:667 |
| [3] | Degischer H P.Mater Des,1997;18:221 |
| [4] | Armin F,Eckhard P,Jorg W.Adv Eng Mater,2002;2:471 |
| [5] | Goddard D M.Met Prog,1984;125:49 |
| [6] | Carolin K,Wolgang S,Markus O,Robert F S.Adv Eng Mater,2000;6:327 |
| [7] | Wu F,Zhu J.Acta Metall Sin,1998;34:449(武风,朱静.金属学报,1998;34:449) |
| [8] | Hufenbach W,Andrich M,Langkamp A,Czulak A.J Mater Process Technol,2006;175:218 |
| [9] | Russell S M,Todd R,Papakyriacou M.Surf Interface Anal,2005;37:336 |
| [10] | Russell S M,Todd R,Papakyriacou M.Mater Sci Eng,2005;A397:249 |
| [11] | McCartney L N,Kelly A.Compos Sci Technol,2007;67:646 |
| [12] | Korab J,Stefanik P,Kavecky S,Sebo P,Korb G.Composites,2002;33A:133 |
| [13] | Stefanik P,Kavecky S,Korb G,Groboth G,Sebo P.J Mater Sci Lett,1997;16:392 |
| [14] | Wolff E G,Min B K,Kural M H.J Mater Sci,1985;20:1141 |
| [15] | Russell S M,Todd R I,Papakyriacou M.J Mater Sci,2006;41:6228 |
| [16] | Korb G,Korab J,Groboth G.Composites,1998;29A:1563 |
| [17] | Wang H H,Li X G,Fei Z M.Aerosp Mater Technol,1995;25(1):41(王鸿华,李贤淦,费铸铭.宇航材料工艺,1995;25(1):41) |
| [18] | Taylor R E.Int J Thermophys,1991;12:723 |
| [19] | Hufenbach W,Andrich M,Langkamp A,Czulak A.J Mater Process Teehnol,2006;175:218 |
| [20] | Rupnowski P,Gentz M,Sutter J K,Kumosa M.Composites,2005;36A:327 |
| [21] | Wang N.Master Degree Dissertation,Harbin Institute of Technology,2007(王宁.哈尔滨工业人学硕上学位论文,2007) |
| [22] | Rojstaczer S,Cohn D,Marom G.J Mater Sci Lett,1985;4:1233 |
| [23] | Rajendra U,Chawla K K.Compos Sci Technol,1994;50:13 |
| [24] | Karadeniz Z H,Kumlutas D.Compos Struct,2007;78:1 |
| [25] | Kelly A,Steam R J,McOartney L N.Compos Sci Technol,2006;66:154 |
| [26] | Zhang Q,Wu G H,Jiang L T,Chen G Q.Mater Chem Phys,2003;81:780 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%