采用Al-Mg-Se-Zr焊丝为填充材料对Al-Mg-Sc合金薄板进行手工非熔化极惰性气体保护焊(TIG焊),并对焊接接头进行350℃下保温1h的焊后热处理.通过拉伸实验、显微硬度测试、SEM及TEM观察对热处理前、后的Al-Mg-Sc合金焊接接头的力学性能及微观组织进行了对比研究.结果表明:热处理前焊接接头强度为332MPa;经350℃/1h热处理后,焊接接头强度增至410 MPa,焊接接头强度系数达到0.98,焊接接头延伸率由5.6%增加至14.4%,并且焊缝区的显微硬度得到大幅度提高,拉伸时断裂位置由焊缝区转移到了熔合区.焊后热处理使焊缝区析出大量弥散分布的Al3(Sc,Zr)粒子,这些粒子与基体共格,使焊缝区的硬度、抗拉强度和屈服强度大幅度提高.
参考文献
| [1] | Smola B,Stulikova I,Ocenasek V,Peleova J,Neubert V.Mater Sci Eng,2007;A462:370 |
| [2] | Jiang F,Yin Z M,Huang B Y,He Y H,Chen S L.J Rare Earths,2004;22:600 |
| [3] | Jiang F,Yin Z M,Huang B Y,He Y H,Chen S L.2004 International Conference on Rare Earth Research and Application(ICRERA-2004),Baotou,China,Aug 8-12,2004:156 |
| [4] | Munoz A C,Ruckert G,Huneau B,Sauvage X,Marya S.J Mater Process Technol,2008;197:337 |
| [5] | Jiang F,Chen S L,Huang B Y,Yin Z M,He Y H.J Cent South Univ Technol,2005;12(Suppl.1):23 |
| [6] | Nie B,Yin Z M,Zhu D P,Jiang F,He Z B.Chin J Rare Earths,2006;30:213(聂波,尹志民,朱大鹏,姜锋,何振波.稀有金属,2006;30:213) |
| [7] | Zhou C R,Pan Q L,Liu X Y.Mater Rev,2006;20:147(周昌荣,潘青林,刘心宇.材料导报,2006;20:147) |
| [8] | Li S L,Pan Q L,Chen X M.Ordnance Mater Sci Eng,2003;26(1):11(李绍禄,潘青林,陈显明.兵器材料科学与工程,2003;26(1):11) |
| [9] | Zhang Y H,Yin Z M.Rare Met Mater Eng,2002;31:167 |
| [10] | Yin Z M,Zhu D P,Jiang F.J Mater Eng,2004;(6):3(尹志民,朱大鹏,姜锋.材料工程,2004;(6):3) |
| [11] | He Z B.Light Alloy Fabr Technol,2006;34(8):44(何振波.轻合金加工技术,2006;34(8):44) |
| [12] | Lapasset G,Girard Y.Mater Sci Forum,2003;426-432:2987 |
| [13] | Wamura S,Nakayama M,Miura Y.Mater Sci Forum,2002;396-402:1151 |
| [14] | Murray J.J Phase Equilib,1998;19:380 |
| [15] | Chen S L,Jiang F,Yin Z M,Lei X F,Nie B.Chin J Nonferrous Metals,2006;16:835(陈苏里,姜锋,尹志民,雷学锋,聂波.中国有色金属学报,2006;16:835) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%