设计了低碳钢激光点焊工艺,显示了小尺寸液态熔池均匀回缩的凝同过程,以此作为平台,进行了焊接熔池表面温度与凝固速率测量方法的研究.采用红外测温仪从熔池表面直接获取熔池凝固过程温度曲线;利用金属固相与液相表面发射率的差异从熔池凝固温度曲线中提取能准确反映液-固转变的特征信息,以此推算了熔池表面的凝固速率;并通过进一步的工艺实验,验证了凝固速率与焊点背面直径之间的良好对应关系.该方法亦适用于其它热加工过程金属凝固速率的测量与分析.
参考文献
| [1] | Garzon C M,Gomes J,Brandi S D.Proc 7th Int Conf Trends in Welding Research,Materials Park,OH:ASM International,2005:951 |
| [2] | David S A,Babu S S,Vitek J M.JOM,2003; 55(6):14 |
| [3] | Hu B,Richardson I M.Proc 24th Int Congress on Application of Lasers and Electro-Optics,Orlando,FL:LaserInstitute of America,2005:1042 |
| [4] | De A,Walsh C A,Maiti S K,Bhadeshia H K D H.Sci Technol Weld Joining,2003; 8:391 |
| [5] | Liu L M,Chi M S,Huang R S,Song G,Zhou Y.Sci China,2005; 48E:706 |
| [6] | Grabas B,Dard-Thuret J,Laurent M,Pelletier J M.Proc 15th Int Congress on Application of Lasers and Electro-Optics.Orlando,FL:Laser Institute of America,1996:36 |
| [7] | Lee M-Y,Kim J-W.Key Eng Mater,2004; 270:2308 |
| [8] | Li Y H,Sun X G,Yuan G B.Opt Precis Eng,2007; 15:1336(李云红,孙晓刚,原桂彬.光学精密工程,2007;15:1336) |
| [9] | Cui Z S.Temperature Computation and Measurement.Beijing:China Metrology Press,1998:163(崔志尚.温度计量与测试.北京:中国计量出版社,1998:163) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%