通过真空熔炼和气体保护,采用熔融玻璃与循环过热相结合的深过冷快速凝固技术,研究了影响富Fe端Fe-B共晶合金熔体净化效果的主要因素,确定了该合金熔体获得超过冷的净化方法,并使Fe83B17共晶合金熔体稳定获得了300-460 K的超过冷度,使Fe80B20过共晶合金熔体的过冷度达到了485 K,从而使Re-B共晶系合金熔体开始形核前的初始过冷度达到了0.3Tm-0.4Tm的水平.通过对冷却曲线的分析,讨论了表征超过冷快速凝固的热力学特征.
参考文献
| [1] | Herlach D M.Mater Sci Eng,1994; R12:177 |
| [2] | Wilde G,Gorler G P,Willnecker R.Appl Phys Lett,1996; 69:2995 |
| [3] | Yang C L,Yang G C,Lu Y P,Chen J Q,Zhou Y H.Acta Metall Sin,2005; 41:1053(杨长林,杨根仓,卢-平,陈甲琪,周尧和.金属学报,2005;41:1053) |
| [4] | Yang C L,Yang G C,Liu F,Chen Y Z,Liu N,Chen D,Zhou Y H.Physics,2006; 373B:136 |
| [5] | Yang C L,Liu F,Yang G C,Chen Y,Liu N,Zhou Y H.Appl Phys,2007; 86A:231 |
| [6] | Hu H Q.Principle of Metal Solidification.2nd ed,Beijing:China Machine Press,2000:256(胡汉起.金属凝固原理.第2版,北京:机械工业出版社,2000:256) |
| [7] | Kui H W,Greer A L,Turnbull D.Appl Phys Lett,1984; 45:615 |
| [8] | Zhou Y H,Hu Z Q,Ji W Q.Solidification Technology.Beijing:China Machine Press,1998:45(周尧和,胡壮麒,介万奇.凝固技术.北京:机械工业出版社,1998:45) |
| [9] | Wei B B.PhD Thesis,Northwestern Polytechnical University,Xi'an,1989(魏炳波.西北工业大学博士学位论文,西安,1989) |
| [10] | Powell G L F.TMS-AIME,1968; 242:2133 |
| [11] | Kattamis T Z,Flemings M C.Trans TMS-AIME,1966; 236:1523 |
| [12] | Zhang Z Z.PhD These,Northwestern Polytechnical University,Xi'an,2000(张振忠.西北工业大学博士学位论文,西安,2000) |
| [13] | Perepezko J H.Mater Sci Eng,1997; A226-228:374 |
| [14] | Singh R N,Jaju R P,Ali I.Physics,2001; 299B:108 |
| [15] | Pan S Q.New Glass.Shanghai:Tongji University Press,1992:30(潘守芹.新型玻璃.上海:同济大学出版社,1992:30) |
| [16] | Battezzati L,Antonione C,Baricco M.J Alloys Cempd,1997; 247:16 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%