在Watt镀液中加入玻璃球,玻璃球以不同频率垂直撞击试样表面形成机械研磨.考察了震荡频率和球直径对镍镀层晶粒细化的影响以及机械研磨对晶粒生长的影响.SEM表面观察表明,机械研磨改变了镀层晶粒的生长方式,使镀层晶粒明显细化,镀层表面光滑.在电沉积过程中施加机械研磨,玻璃球的撞击会在镀层表面产生宏观和微观缺陷,增加形核中心,提高形核速率;玻璃球撞击晶粒尖端,使得镀层表面变得平整,有利于电力线均匀分布,促进形核,避免了晶粒不均匀长大.
参考文献
| [1] | Sato M,Tsuji N,Minamino Y,Koizumi Y.Sci Technol Adv Mater,2004; 5:145 |
| [2] | Tao N R,Wang Z B,Tong W P,Sui M L,Lu J,Lu K.Acta Mater,2002; 50:4603 |
| [3] | Lu K,Lu J.Mater Sci Eng,2004; A375:38 |
| [4] | Umemoto M,Todaka K,Tsuchiya K.Mater Sci Eng,2004; A375:899 |
| [5] | Tao N R,Sui M L,Lu J,Lu K.Nanostruct Mater,1999;11:433 |
| [6] | Liu G,Lu J,Lu K.Mater Sci Eng,2000; A286:91 |
| [7] | Akamatsu H,Ikeda T,Azuma K,Fujiwara E,Yatsuzuka M.Surf Coat Technol,2001; 136:269 |
| [8] | Tong W P,Tao N R,Wang Z B,Lu J,Lu K.Science,2003; 299:5607 |
| [9] | Gu J F,Bei D H,Pan J S,Lu J,Lu K.Mater Lett,2002; 55:340 |
| [10] | Zhan Z L,He Y D,Wang D R,Gao W.Intermetallics,2006; 14:75 |
| [11] | Gordon M.Met Finish,2002; 100:384 |
| [12] | Ning Z H,He Y D,Gao W.Surf Coat Technol,2008; 202:2139 |
| [13] | El-Sherik A M,Erb U,Page J.Surf Coat Technol,1996;88:70 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%