采用基于密度函数理论的全势线性缀加平面波(FPLAPW)和超晶胞方法,研究了加入Fe元素对富镍NiAl金属间化合物晶格常数、磁性和剪切模量以及电子结构的作用规律.结果表明,随着Fe元素的增加,Ni62.5-xAl37.5Fex(x=0,6.25,12.5)金属间化合物的磁矩显著增大;Fe原子的磁性使Ni62.5-xAl37.5Fex化合物的晶格膨胀,并明显降低了化合物的切变模量.还就Ni62.5-xAl37.5Fex化合物电子结构的计算结果进行了讨论.
参考文献
| [1] | Liu C T,Fu C L,Chisholm M F,Thompson J R,Krcmar M,Wang X-L.Prog Mater Sci,2007; 52:352 |
| [2] | Liu C T,Fu C L,Pike L M,Easton D S.Acta Mater,2002;50:3203 |
| [3] | Fu C L,Liu C T,Wang X L,Krcmar M,Fernandez-Baca J A.Intermetallics,2004; 12:911 |
| [4] | Uwakweh O N C,Liu C T.Intermetallics,2007; 15:98 |
| [5] | Yang L,Wang X L,Liu C T,Fernandez-Baca J A,Fu C L,Richardson J W,Shi D.Scr Mater,2007; 56:911 |
| [6] | Pike L M,Chang Y A,Liu C T.Intermetallics,1997; 5:601 |
| [7] | Guo G Y,Wang H H.Phys Rev,2000; 62B:5136 |
| [8] | Liu A Y,Singh D J.Phys Rev,1993; 47B:8515 |
| [9] | Schwarz K,Blaha P,Madsen G K H.Comput Phys Commun,2002; 147 (1-2):71 |
| [10] | Mehl M J,Klein B M,Papaconstantopoulos D A.In:Westbrook J H,Fleischer R L,eds.,Intermatllic Compounds,Vol.1:Principles,London:John Wiley & Sons Ltd,1994:195 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%