用等离子喷涂法成功制备了SiCp/FeS复合涂层,SiC颗粒尺寸为纳米级,均匀分布于FeS基体,涂层和40Cr钢基体结合良好.研究了FeS涂层和SiCp/FeS复合涂层的摩擦学性能.结果表明,SiCp/FeS复合涂层兼具优良的减摩性能和耐磨性能.在干摩擦条件下,掺入质量分数为0.2和0.3的纳米SiC颗粒时,摩擦系数和FeS涂层接近,但表面磨损体积显著降低,降幅可达1个数量级;油润滑条件下,SiCp/FeS复合涂层的摩擦系数低于FeS涂层,复合涂层具有比FeS涂层更佳的减摩性能.
参考文献
| [1] | Rapoport L,Leshinsky V,Lapsker I,Volovik Y,Nepomnyashcky O,Lvovsky M,Popovitz-Biro R,Feldman Y,Tenne R.Wear,2003; 255:785 |
| [2] | Wang H D,Zhuang D M,Wang K L,Liu J J,Fang X D,Li Y L.Acta Metall Sin,2003; 39:1031(王海斗,庄大明,王昆林,刘家浚,方晓东,李永良.金属学报,2003;39:1031) |
| [3] | Chen Y X,Feng Z Z,Liu W M.Tribology,2002; 22(2):85(陈云霞,冯治中,刘维民.摩擦学学报,2002;22(2):85) |
| [4] | Lee I,Park I.Surf Coat Technol,2006; 200:3540 |
| [5] | Chen Y X,Wang B,Liu W M.J Process Eng,2002; 2:365(陈云霞,王博,刘维民.过程工程学报,2002;2:365) |
| [6] | Cosemans P,Zhu X,Gelis J P,Stappen M V.Surf Coat Technol,2003; 174-175:416 |
| [7] | Goller R,Torri P,Baker M A,Gilmore R,Gissler W.Surf Coat Technol,1999; 120-121:453 |
| [8] | Wang C M.Master Dissertation,Southeast University,Nanjing,2005(王春明.东南大学硕士学位论文,南京,2005) |
| [9] | Xu T,Zhao J Z,Xu K.Tribol Trans,1997; 40; 178 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%