在温度梯度为200 K/cm和凝固速率为2-10μm/s下, Cu-1.0%Cr亚共晶合金的凝固组织中分别存在单相平界面和共晶、单相平界面和胞晶及胞间共晶、单相胞晶和共晶3种带状组织.从实验和理论两方面阐明了上述带状组织的产生与合金定向凝固界面前沿的溶质分布有关;形成的原因是合金未达到稳态凝固,凝固速率和合金成分一直处于变化之中.另外,单相平界面和共晶的带状组织中,合金凝固速率在单相平界面凝固中随着界面液相成分的增加而逐渐增大,而在共晶组织中随着界面前沿液相成分的减少而逐渐减小.
参考文献
| [1] | Burden M H,Hunt J D.J Cryst Growth,1974; 22:109 |
| [2] | Karma A,Sarkissian A.Metall Mater Trans,1996; 27A:635 |
| [3] | Hunziker O,Vandyoussefi M,Kurz W.Acta Mater,1998;46:6325 |
| [4] | Kerr H W,Kurz W.Int Mater Rev,1996; 41:129 |
| [5] | Han S H,Trivedi R.Metall Mater Trans,2000; 31A:1819 |
| [6] | Karma A,Rappel W J,Fuh B C,Trivedi R.Metall Mater Trans,1998; 29A:1457 |
| [7] | Tokieda K,Yasuda H,Ohnaka I.Mater Sci Eng,1999; A262:238 |
| [8] | Li S M,Liu L,Li X L,Fu H Z.Acta Metall Sin,2004; 40:20 (李双明,刘林,李晓历,傅恒志.金属学报,2004;40:20) |
| [9] | Li X Z,Guo J J,Su Y Q,Wu S P,Fu H Z.Acta Metall Sin,2005; 41:593 (李新中,郭景杰,苏彦庆,吴士平,傅恒志.金属学报,2005;41:593) |
| [10] | Guo J J,Li X Z,Su Y Q,Wu S P,Fu H Z.Acta Metall Sin,2005; 41:599 (郭景杰,李新中,苏彦庆,吴士平,傅恒志.金属学报,2005;41:599) |
| [11] | Liu P,Jia S G,Zhao D M,Ren F Z,Tian B H,Kang B X.Mater Rev,2004; 18(6):32 (刘平,贾淑果,赵冬梅,任凤章,田保红,康布熙.材料导报,2004;18(6):32) |
| [12] | Bi X Q,Hu R,Li J S,Zhu Q,Fu H Z.Mater Sci Technol,2005; 13:153 (毕晓勤,胡锐,李金山,朱琦,傅恒志.材料科学与工艺,2005;13:153) |
| [13] | Hu R,Bi X Q,Li J S,Fu H Z.Sci Technol Adv Mater,2005; 6:950 |
| [14] | Carroll H E,Whitehouse A F.Scr Mater,2000; 42:1133 |
| [15] | Yu J Q,Yi W Z,Chen B D,Chen H J.Phase Diagram of Binary Alloy.Shanghai:Shanghai Science and Technology Press,1987:318 (虞觉奇,易文治,陈邦迪,陈宏鉴.二元合金相图集.上海:上海科学技术出版社,1987:318) |
| [16] | Tiller W A,Jackson K A,Rutter J W,Chalmers B.Acta Metall,1953; 1:428 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%