采用区熔定向凝固方法,先以30 mm/h低速生长,再以480 mm/h高速生长,制备了磁致伸缩性能较为均匀的《110》取向Tb0.36Dy0.64(Fel-xCox)2(x=0,0.1,0.15)合金棒.研究了不同晶体生长阶段的轴向择优取向和微观组织对磁致伸缩性能的影响.结果表明,轴向择优取向度主要影响样品在无预压应力条件下的磁致伸缩性能;富稀土相分布主要影响样品在施加预压应力条件下的磁致伸缩性能.沿合金棒轴向,从底部到顶部择优取向度逐渐增高,富稀土相由网状分布变为平行排列,造成合金棒顶部和中部的磁致伸缩性能较底部更高.磁化场为240 kA/m时磁致伸缩不均匀度小于6%,显示了良好的均匀性.
参考文献
| [1] | Clark A E.Ferromagnetic Materials.Vol.1,Amsterdam:North-Holland,1980:531 |
| [2] | Verhoeven J D,Gibson E D,McMasters O D,Ostenson J E.Metall Trans,1990;21A:2249 |
| [3] | Jiang C B,Zhao Y,Xu H B.Acta Metall Sin,2004;40:373(蒋成保,赵岩,徐惠彬.金属学报,2004;40:373) |
| [4] | Zhao Y,Jiang C B,Zhang H,Xu H B.J Alloy Compd,2003;354:263 |
| [5] | Shi Z X,Chen Z M,Wang X H,Lin M H,Zhang Y M.J Alloy Compd,1997;258:30 |
| [6] | Zhang M C,Gao X X,Zhou S Z,Shi Z X.J Alloy Compd,2004;381:226 |
| [7] | Ma TY,Jiang C B,Xu H B.Appl Phys Lett,2005;86:162505 |
| [8] | Mei W,Okane T,Umeda T,Zhou S Z.J Alloy Compd,1997;248:151 |
| [9] | Ma TY,Jiang C B,Xu X,Zhang H,Xu H B.J Magn Magn Mater,2005;212:317 |
| [10] | Mei W,Umeda T,Zhou S Z,Wang R.J Alloy Compd,1995;224:76 |
| [11] | Clark A E,Teter J P,McMasters O D.J Appl Phys,1988;63:3910 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%