对Fe78Si9B13非晶进行了低频磁脉冲处理(场强0.01-0.04 T,频率20-40 Hz,作用时间60-300 s),以红外非接触测温仪测量处理过程的试样温升,用M(o)ssbauer谱、透射电镜观察试样的微结构变化.研究表明,在磁脉冲作用下,非晶合金发生了低温纳米晶化(温升△T=7℃),晶化相α-Fe(Si)的晶粒尺寸约10 nm、析出量2.18%-9.43%;所形成的双相纳米合金对应的平均超精细磁场较非晶的原始制备态明显增加.
参考文献
| [1] | Lu K,Zhou F.Acta Metall Sin,1997; 33:99(卢柯,周飞.金属学报,1997;33:99) |
| [2] | Wu W F,Yao K F.Rere Met Mater Eng,2005; 34:505(吴文飞,姚可夫.稀有金属材料与工程,2005;34:505) |
| [3] | Kulik T,Horubata T,Matyja H.Mater Sci Eng,1992;A157:107 |
| [4] | Qi M,Wang Y,Wang Y N,Yang D Z.J Funct Mater,2005; 36(1):35(齐民,王岩,王轶农,杨大智.功能材料,2005;36(1):35) |
| [5] | Yoshizawa Y,Oguma S,Yamauchi K.J Appl Phys,1988;64:6044 |
| [6] | Long Y,Zhang Z Y,Li S W.Functional Magnetic Materials and Its Applications.Beijing:China Machine Press,1997:115(龙毅,张正义,李守卫.功能磁性材料及其应用.北京:机械工业出版社,1997:115) |
| [7] | Tong H Y,Wang J T,Ding B Z,Jiang H G,Lu K.J Non-Cryst Solids,1992; 150:444 |
| [8] | Vazquez M,Marin P,Leccabue F,Watts B E,Deriu A,Negri D,Bocelli G.IEEE Trans Magn,1993; 29:2685 |
| [9] | Chao Y S,Li M Y,Geng Y,Liu J G.Acta Phys Sin,2004;53:3453(晁月盛,李明扬,耿岩,刘吉刚.物理学报,2004;53:3453) |
| [10] | Rbulsala A,Gammaitoni L.Phys Today,1996:39 |
| [11] | Shao Y Z,Zhong W R,Lin G M,Li J C.Acta Phys Sin,2004; 53:3157(邵元智,钟伟荣,林光明,李坚灿.物理学报,2004;53:3157) |
| [12] | Gibb T C.Principles of M(o)ssbauer Spectroscopy.London:Chapman and Hall,1976:41 |
| [13] | Guo Y C,Wang Z X.The Physics of Noncrystal State.Beijing:Science Press,1984:175(郭贻诚,王震西.非晶态物理学.北京:科学出版社,1984:175) |
| [14] | Tong H Y,Ding B Z,Wang J T,Lu K.J Appl Phys,1992;72:5124 |
| [15] | Lai Z H,Conrad H,Chao Y S,Wang S Q,Sun J.Scr Metall,1989; 23:305 |
| [16] | Lai Z H,Conrad H,Teng G Q,Chao Y S.Mater Sci Eng,2000; A287:238 |
| [17] | Xiao S H,Chao Y S,Zhou B L.Acta Phys Sin,2000; 49:288(肖素红,晁月盛,周本廉.物理学报,2000;49:288) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%