对[001]取向镍基单晶合金进行预压缩处理,获得P-型筏状结构后进行拉伸蠕变实验,测定P-型γ'合金(预压缩态)与立方γ'合金(热处理态)的相对蠕变性能.结果表明:在800 ℃,600 MPa条件下,P-型γ'合金的初期蠕变应变及稳态蠕变速率相对较高,而持久寿命相对较短.TEM观察显示,P-型γ'合金在蠕变初始阶段除了基体中的{111}<110>多滑移启动外,位错还以层错和超位错的形式切入γ'相.在980-1020℃温度区间及恒定载荷200 MPa条件下,P-型γ'合金的稳态蠕变速率相对较低,持久寿命相对较高.在稳态蠕变初期,合金中的γ'相有效地抑制了位错沿垂直γ/γ'界面的攀移运动;而在稳态蠕变中期,γ'相被稠密的位错网包围,位错难以切入,合金的蠕变抗力提高.
参考文献
| [1] | Feller-Kniepmeier M,Kuttner T.Acta Metall Mater,1994; 42:3167 |
| [2] | Nathal M V,MacKay R A,Miner R V.Metall Trans,1989; 20A:133 |
| [3] | Pearson D D,Lemkey F D,Kear B H.In:Tien J K,Wlodek S T,Morrow H Ⅲ,Gell M,Maurer G E,eds.,Superalloys 1980,Metals Park,OH:ASM,1980:513 |
| [4] | Pearson D D,Kear B H,Lemkey F D.In Creep and Fracture of Engineering Materials and Structure.Swansea,UK:Pineridge Press,1983:213 |
| [5] | Caron P,Khan T.Mater Sci Eng,1983; A61:173 |
| [6] | Guo J T,Ranucci D,Picco E,Strocchi P M.Metall Trans,1983; 14A:2329 |
| [7] | Milligan W W,Antolovich S D.Metall Trans,1991; 22A:2309 |
| [8] | Condat M,Décamps B.Scr Metall,1987; 21:607 |
| [9] | Ha K F.Microscopic Theory of Metal Mechanical Properties.Beijing:Science Press,1983:520(哈宽富.金属力学性质的微观理论.北京:科学出版社,1983:520) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%