采用定量金相及化学分析方法研究了B,Sr联合处理对亚共晶Al-7Si合金凝固组织的影响.Al-7Si合金熔体经B,Sr联合处理时,Sr对合金的细化处理效果无明显影响.而B的出现减少了熔体中有效Sr含量,降低了合金的变质处理效果.在此基础上,结合冷却曲线模式识别技术研究了合金熔体状态与冷却曲线凝固段整体形状的关系.随着表征曲线相似程度的综合偏差值Ω趋近于零,相应的变质级别差值及晶粒尺寸差值也同时向零收敛.冷却曲线凝固段的整体形状可以表征B,Sr联合处理后合金的熔体状态.通过建立基于大量实验结果累积的数据库,有望实现B,Sr联合处理Al-7Si合金细化变质效果的在线评测.
参考文献
| [1] | Croseley E,Mondolfo L F.AFS Trans,1966; 74:53 |
| [2] | Argyropoulos S,Closset B,Oger H.AFS Trans,1983; 27:351 |
| [3] | Paray F,Gruzleski J E.AFS Trans,1994; 115:833 |
| [4] | Apelian D,Sigworth G K,Wharler K R.AFS Trans,1984;92:297 |
| [5] | Kori S A,Murty B S,Chakraborty M.Mater Sci Eng,2000; A283:94 |
| [6] | Kurfman V B.AFS Trans,1961; 69:234 |
| [7] | Charbonnier J.Hommes Foerie,1975; 59:29 |
| [8] | Ananthanarayanan L,Samuel F H,Gruzleski J E.AFS Trans,1992; 113:383 |
| [9] | Easton M,Stjohn D.Metall Mater Trans,1999; 30A:1613 |
| [10] | Charbonnier J.AFS Trans,1984; 92:907 |
| [11] | Bekaert F,Ghent E W.Aluminum,1996; 72:442 |
| [12] | Gong L Q.Spec Cast Nonferrous Alloys,1996; 1:16(龚磊清.特种铸造及有色合金,1996;(1):16) |
| [13] | Tenekedjiev N and Gruzleski J E.AFS Trans,1991; 35:1 |
| [14] | Li Y X,Wang Q,Xu X R.Mater Rev,2002; 16:1(李言祥,王强,徐雪蓉.材料导报,2002;16:1) |
| [15] | Li Y X,Hu X,Xu X R.J Mater Sci Technol,2001; 17:73 |
| [16] | Li Y X,Xu X R,Wang Q,Liu B C.Int J Cast Met Res,2003; 16:41 |
| [17] | Wang Q,Li Y X,Li X C.Metall Mater Trans,2003; 34A:1175 |
| [18] | Li Y X,Geng H Y.Spec Cats Nonferrous Alloys,2004;(6):4(李言祥,耿慧远.特种铸造及有色合金,2004;(6):4) |
| [19] | Geng H Y,Li Y X,Chen X,Wang X.Scr Mater,2005;53:69 |
| [20] | Chen X,Geng H Y,Li Y X.Acta Metall Sin,2005; 41:891(陈祥,耿慧远,李言祥.金属学报,2005;41:891) |
| [21] | Nogita K,McDonald S D,Dahle A K.Mater Trans,2003;44:692 |
| [22] | Sigworth G K,Guzowski M M.AFS Trans,1985; 93:907 |
| [23] | Geng H Y.PhD Dissertation,Tsinghua University,Beijing,2005(耿慧远.清华大学博士学位论文,北京,2005) |
| [24] | Liao H C,Sun G X.Scr Mater,2003; 48:1035 |
| [25] | Li J G,Zhang B Q,Wang L,Yang W Y,Ma H T.Mater Sci Eng,2002; A328:169 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%