利用分子动力学方法对非晶纯镍材料压缩变形过程中纳米晶化现象进行了模拟,研究了非晶变形过程中绝热温升对非晶晶化的影响,结果表明,绝热温升不是导致非晶晶化的主要因素.从微观结构演化的角度考察了非晶晶化过程中晶粒的形核和长大,分析发现,应变导致非晶态金属从亚稳态结构逐渐向稳态结构转变,在系统内部的部分短程序原子团逐步合并形成小的晶核,随着应变的增加,晶核逐渐长大,形成一定尺寸的纳米晶粒.
参考文献
| [1] | Inoue A.Acta Mater,2000; 48:279 |
| [2] | Johnson W L.MRS Bull,1999; 24:42 |
| [3] | Loffler J F.Intermetallics,2003; 11:529 |
| [4] | Zhang Z F,Eckert J,Schultz L.Acta Mater,2003; 51:1167 |
| [5] | Chen H,He Y,Shiflet G J,Poon S J.Nature,1994; 367:541 |
| [6] | Jiang W H,Atzmon M.Acta Mater,2003; 51:4095 |
| [7] | Kim J J,Choi Y,Suresh S,Argon A S.Science,2002; 295:654 |
| [8] | Hebert R J,Perepezko J H.Mater Sci Eng,2004; A375-377:728 |
| [9] | Baskes M I.Phys Rev,1992; 46B:2727 |
| [10] | Daw M S,Baskes M I.Phys Rev Lett,1983; 50:1285 |
| [11] | Daw M S,Baskes M I.Phys Rev,1984; 29B:6443 |
| [12] | Qi L,Zhang H F,Hu Z Q.Acta Metall Sin,2004; 40:736(戚力,张海峰,胡壮麒.金属学报,2004;40:736) |
| [13] | Honeycutt J D,Andersen H C.J Phys Chem,1987; 91:4950 |
| [14] | Lu K,Wang J T.Acta Metall Sin,1991; 27:38(卢柯,王景唐.金属学报,1991;27:38) |
| [15] | Qi Y,Cagin T,Kimura Y,Goddard W A Ⅲ.Phys Rev,1999; 59B:3527 |
| [16] | Schuh C A,Lund A C.Nat Mater,2003; 2:449 |
| [17] | Shi Y F,Falk M L.Appl Phys Lett,2005; 86:011914 |
| [18] | Lu K,Wang J T,Dong L.Acta Metall Sin,1991; 27:31(卢柯,王景唐,董林.金属学报,1991;27:31) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%