在Gleeble-1500热模拟机上对Ni76Cr19AlTi合金棒材进行恒温和恒速压缩变形实验,变形温度范围为800-1150℃,应变速率范围为10-3-100s-1.结果表明,实验合金在800和850℃热压缩时变形抗力较大,容易发生开裂;而在950-1150℃温度范围内热变形由于发生动态再结晶,合金变形抗力减小,变形容易进行,不会发生开裂.研究了合金在高温塑性变形过程中流变应力的变化规律,确定了合金在950-1150℃范围内的变形激活能Q为376.84 kJ/mol,应力指数n为4.15.对合金的热压缩变形真应力-真应变曲线及变形机制的分析表明,合理的变形条件为1050-1150℃及10-1-100s-1.
参考文献
| [1] | Srinivasan N,Prasad Y V R K.J Mater Process Technol,1995; 51:171 |
| [2] | Choudhury I A,El-Baradie M A.J Mater Process Technol,1998; 77:278 |
| [3] | Gabrisch H,Mukherji D.Acta Mater,2000; 48:3157 |
| [4] | Tian B,Paris O,Zickler G A,Lind C,Wasle G,May R P.Scr Mater,2002; 47:25 |
| [5] | Nembach E,Pesicka J,Langmaack E.Mater Sci Eng,2003; A362:264 |
| [6] | Kim D K,Kim D Y,Ryu S H,Kim D J.J Mater Process Technol,2001; 113:148 |
| [7] | Hagiwara Y,Ishida M,Oka T,Watanabe R,Sato K.SAE Trans,1991; 100:484 |
| [8] | Takagi Y,Okabe M,Likubo T.Stahl Eisen,1990; (Spec):138 |
| [9] | Zener C,Hollomon J H.J Appl Phys,1944; 15(1):22 |
| [10] | Sellars C M.Acta Metall,1966; 14:1136 |
| [11] | Sellars C M,Tegart W J.Int Metall Rev,1972; 17:1 |
| [12] | Bruni C,Forcellese A,Gabrielli F.J Mater Process Technol,2002; 125-126:242 |
| [13] | Prasad Y V R K,Sasidhara S,Sikka V K.Intermetallics,2000; 8:987 |
| [14] | Park N K,Kim I S,Na Y S,Yeom J T.J Mater Process Technol,2001; 111:98 |
| [15] | Zhang B J,Zhao G P,Jiao L Y,Xu G H,Qin H Y,Feng D.Acta Metall Sin,2005; 41:351(张北江,赵光普,焦兰英,胥国华,秦鹤勇,冯涤.金属学报,2005;41:351) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%