研究了一种抗热腐蚀高温合金K44在800,850和900℃经(1-10)×103h长期时效后γ'相的变化和拉伸性能.结果表明,γ'沉淀相的长大动力学符合Lifshitz-Slyozof-Wagner熟化规律,长大激活能为255 kJ/mol.相对较小的γ'相出现与弹性应变能相关的形态不稳定现象.合金屈服强度随时效温度升高和时效时间的延长而降低,可以由Labusch-Schwarz强化理论来解释,但塑性却出现了波动.合金的强化机制为强相互作用位错对的切割机制.
参考文献
| [1] | Nembach E.Particle Strengthening for Metals and Alloys.New York:John Wiley & Sons,1997:230 |
| [2] | Reppich B,Schepp P,Wehner G.Acta Metall,1982; 30:95 |
| [3] | Brown L M,Ham R K.In:Kelly A,Nicholson R B,eds.,Strengthening Methods in Crystals,Amsterdam:Elsevier,1971:9 |
| [4] | Ardell A J.Met Trans,1985; 16A:2131 |
| [5] | Hou J S,Zhang Y L,Guo J T,Ji G,Zhou L Z,Ye H Q.Acta Metall Sin,2004; 40:579(侯介山,张玉龙,郭建亭,冀光,周兰章,叶恒强.金属学报,2004;40:579) |
| [6] | Lifshitz I M,Slyozov V V.J Phys Chem Solids,1961; 19:35 |
| [7] | Wagner C Z.Elektrochem,1961; 65:581 |
| [8] | Stevens R A,Flewitt P E J.Mater Sci Eng,1979; 37:237 |
| [9] | Baldan A.J Mater Sci,2002; 37:2379 |
| [10] | Yoo Y S.Scr Mater,2005; 53:81 |
| [11] | Narayan V.http://www.msm.cam.ac.uk/map /data/neural/lattmisfit-b.html.University of Cambridge,1999 |
| [12] | Pollock T M,Argon A S.Acta Metall Mater,1991; 40:1 |
| [13] | Fior N F.High Temp Mater,1975; 2:373 |
| [14] | Guo S R,Lu D Z,Guo J T.Acta Metall Sin,1998; 34:482(郭守仁,卢德忠,郭建亭.金属学报,1998;34:482) |
| [15] | Morinaga M,Yukawa N,Ezaki H.Philos Mag,1995; 51A:223 |
| [16] | Durrand-Charre M.The Microstructure of Superalloys.Amsterdam:Gordon and Breach Science Publishers,1997:1 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%