通过研究Fe-10Al,Fe-5Cr-10Al和Fe-10Cr-10Al(原子分数,%)合金在900℃的氧化行为,分析了二元Fe-Al合金形成选择性氧化铝膜所需的临界铝浓度.讨论了三元Fe-Cr-Al合金形成保护性氧化膜的机理,对于不发生Al的内氧化的情况,提出合金中第三组元Cr的作用机制的新解释.
参考文献
| [1] | Hindam H, Whittle D P. Oxid Met, 1982; 18:245 |
| [2] | Tomaszewicz P, Wallwork G R. Oxid Met, 1983; 20:75 |
| [3] | Boggs W E. J Electrochem Soc, 1971; 118:906 |
| [4] | Hagel W C. Corrosion, 1965; 21:316 |
| [5] | Ahmed H A, Smeltzer W W. J Electrochem Soc, 1986;133:212 |
| [6] | Saegusa F, Lee L. Corrosion, 1966; 22:168 |
| [7] | Ahmed H A, Underhill R P, Smeltzer W W, Brett M E,Graham M J. Oxid Met, 1987; 28:347 |
| [8] | Tomaszewicz P, Wallwork G R. Oxid Met, 1983; 19:165 |
| [9] | Hou P Y, Stringer J. Oxid Met, 1992; 38:323 |
| [10] | Miner R G, Nagarajan V. Oxid Met, 1981; 16:313 |
| [11] | Stott F H, Wood G C, Hobby M G. Oxid Met, 1971; 3:103 |
| [12] | Golightly F A, Wood G C, Stott F H. Oxid Met, 1980; 14:217 |
| [13] | Lambertin M, Stoklosa A, Smeltzer W W. Oxid Met, 1981;15:355 |
| [14] | Sadique S E, Mollah A H, Islam M S, Ali M M, Megat M H H, Basri S. Oxid Met, 2000; 54:385 |
| [15] | Stott F H, Wood G C, Stringer J. Oxid Met, 1995; 44:113 |
| [16] | Wagner C. Corros Sci, 1965; 5:751 |
| [17] | Zhang Z G, Gesmundo F, Hou P Y, Niu Y. Corros Sci,2005, in press |
| [18] | Wagner C. J Electrochem Soc, 1952; 99:369 |
| [19] | Gesmundo F, Niu Y. Oxid Met, 1998; 50:1 |
| [20] | Crank J. The Mathematics of Diffusion. New York: Oxford University Press, 1994 |
| [21] | Takada J, Yamamoto S, Kikuchi S, Adachi M. Oxid Met,1986; 25:93 |
| [22] | Carslaw H S, Jaeger J C. Conduction of Heat in Solids.New York: Oxford University Press, 1993 |
| [23] | Graham M J, Eldrige J I, Mitchell D F, Hussey R J. Mater Sci Forum, 1989; 43:207 |
| [24] | Niu Y, Gesmundo F. Oxid Met, 2001; 56:517 |
| [25] | Levin E M, Robbins C R, McMurdie H F. Phase Diagrams for Ceramists. Columbus: The American Ceramic Society, 1969 |
| [26] | Niu Y, Gesmundo F. Oxid Met, in press |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%