提高低碳(锰)钢中碳含量,低碳(锰)钢形变强化相变孕育期明显延长,转变动力学曲线整体向高应变方向移动.提高锰含量,相变孕育期有所延长,转变动力学过程明显变缓.提高碳、锰含量,钢中铁素体形核率增大,晶粒细小,碳的影响程度比锰显著.过冷奥氏体形变过程铁素体转变分三个阶段,第一阶段符合Cahn的"位置饱和"机制,第二、三阶段不符合"位置饱和"机制.
参考文献
| [1] | Sun Z Q, Yang W Y, Qi J J, Hu A M. Mater Sci Eng A,2002, 334:201 |
| [2] | Qi J J, Yang W Y, Sun Z Q. J Univ Sci Technol Beijing,2002, 24(2): 97(齐俊杰,杨王玥,孙祖庆.北京科技大学学报,2002,24(2):97) |
| [3] | Yang W Y, Hu A M, Qi J J, Sun Z Q. Chin J Mater Res,2001, 15:171(杨王玥,胡安民,齐俊杰,孙祖庆.材料研究学报,2001,15:171) |
| [4] | Hu A M. Master Thesis, University of Science and Technology Beijing, 2000(胡安民.北京科技大学硕士学位论文.2000) |
| [5] | Qi J J. PhD Thesis, University of Science and Technology Beijing, 2002(齐俊杰.北京科技大学博士学位论文.2002) |
| [6] | Zhou R F,Yang W Y,Sun Z Q.Acta Metall Sin,jn accepted.(周荣锋,杨王玥,孙祖庆.金属学报,已接受) |
| [7] | Zhou R F,Yang W Y,Sun Z Q.Iron Steel,in accepted.(周荣锋,杨王玥,孙祖庆.钢铁,已接受) |
| [8] | Yang P,Fu Y Y,Cui F E,Sun Z Q.Acta Metall Sin,2001,36:617(杨平,傅云义,崔风娥,孙祖庆.金属学报,2001,37:617) |
| [9] | Kamat R G, Hawbolt E B, Brown L C, Brimacombe J K.Met Trans A, 1992, 23A: 2469 |
| [10] | Leslie W C, Rauch G C. Met Trans A, 1978, 9A: 343 |
| [11] | Khlestov V M, Konopleva E V, Mcqueen H J. Can Metall Q, 1998, 26(1): 64 |
| [12] | Hickson M R, Hurley P J, Gibbs R K, Kelly G L, Hodgson P D. Metall Mater Trans A, 2002, 33A: 1019 |
| [13] | Cahn J W. Acta Metall, 1956, 9:449 |
| [14] | Hickson M R, Gibbs R K, Hodgson P D. ISIJ Int, 1999,39:1176 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%