对调质处理的45碳素结构钢进行了应变循环低周疲劳实验以及应力控制棘轮失效实验.对于前者进行了带平均应变和不带平均应变的实验,以研究平均应变对低周疲劳特性的影响;对于后者研究了平均应力和应力幅值对棘轮失效的影响.应变循环实验表明:平均应变对循环饱和行为以及低周疲劳循环失效圈数并没有明显的影响,但对材料的循环初期循环塑性行为有影响.棘轮失效实验结果表明:当应力幅值较大而平均应力较小时,材料的棘轮失效主要归于较大塑性应变幅值引起的低周疲劳破坏;当平均应力较大而应力幅值相对较小时,材料的棘轮失效主要归于较大的棘轮应变引起的材料韧性破坏,其失效准则可以用最大单调极限应变来表征.
参考文献
| [1] | Yoshida F. Int J Press Vessel Piping, 1990, 44:207 |
| [2] | Chaboche J L, Nouailhas D. ASME J Eng Mater Technol,1989, 111:384 |
| [3] | Ruggles M B, Krempl E. ASME J Eng Mater Technol,1989, 111:378 |
| [4] | Ruggles M B, Krempl E. J Mech Phys Solids, 1990, 38:575 |
| [5] | Mizuno M, Mima Y, Abdel-Karim M, Ohno N. ASME J Eng Mater Technol, 2000, 122:29 |
| [6] | Ohno N, Abdel-Karim M, Kobayashi M, Igari T. Int J Plast, 1998, 14:355 |
| [7] | Ohno N, Abdel-Karim M. ASME J Eng Mater Technol,2000, 122:35 |
| [8] | Yang X J, Gao Q, Cai L X, Xiang Y K. Acta Aeronautica et Astronautica Sin, 1997, 18:395(杨显杰,高庆,蔡力勋,向阳开.航空学报,1997,18:395) |
| [9] | Yang X J, Gao Q, Cai L X, Xiang Y K. Mech Solid Sin,1997, 10:359 |
| [10] | Yang X J, Cai L X, Xiang Y K. J Southwest Jiaotong Univ,1998,32:604(杨显杰,蔡力勋,向阳开.西南交通大学学报,1998,32(6):604-610) |
| [11] | Yang X J, Kang G Z, Gao Q, Sun Y F. Acta Metall Sin,1999, 35:698(杨显杰,康国政,高庆,孙亚芳.金属学报,1999,35:698) |
| [12] | Kang G Z, Gao Q, Yang X J. Nuclear Power Eng, 2001,22:324(康国政,高庆,杨显杰.核动力工程,2001,22:324) |
| [13] | Hassan T, Kyriakides S. Int J Plast, 1994, 10:149 |
| [14] | Ringsberg J W. Int J Fatigue, 2001, 23:575 |
| [15] | Jiang Y, Sehitoglu H. Wear, 1999, 224:38 |
| [16] | Jiang Y. Fatigue Fract Eng Mater Struct, 2000, 23:19 |
| [17] | Fatemi A, Yang L. Int J Fatigue, 1998, 20:9 |
| [18] | Jiang Y, Sehitoglu H. Int J Plast, 1994, 10:579 |
| [19] | Skoczen B. ASME J Eng Mater Technol, 1996, 118:387 |
| [20] | Xia Z, Kujawski D, Ellyin F. Int J Fatigue, 1996, 18:335 |
| [21] | Coffin L F. Trans ASME, 1954, 76:931 |
| [22] | Manson S S. National Advisory Commissions on Aeronautics, Report 1170, Cleveland: Lewis Fight Propulation Laboratory, 1954 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%