控制退火处理工艺使Fe73.5Cu1Nb3Si13.5B9非晶合金发生纳米晶化,获得不同晶粒尺度和晶相体积分数的非晶纳米晶双相组织状态.基于铁磁学严格Heisenberg自旋交换模型,构造适合非晶纳米晶双相结构要求的双相自旋团聚点阵.采用MonteCarlo模拟方法对上述双相自旋交换耦合点阵进行数值模拟计算.实验测定了经不同退火处理后双相Fe73.5Cu1Nb3Si13.5B9合金的纳米晶粒大小、纳米晶相所占体积分数以及晶间非晶相厚度对晶间非晶相Curie温度的影响.发现晶间非晶相Curie温度与其厚度的倒数成线性关系.模拟计算与实验测量结果相符.
参考文献
| [1] | Yoshizawa Y, Oguma S, Yamauchi K. J Appl Phys, 1988,64:6044 |
| [2] | Yavari A R, Drbohlav O. Mater Trans JIM, 1995, 26:896 |
| [3] | Makino A, Hatanai T, Inoue A, Masumoto T. Mater Sci Eng, 1997, 226-228A: 594 |
| [4] | He K Y. Metal Funct Mater (Suppl), 1998, 5:10(何开元.金属功能材料(增刊),1998,5:10) |
| [5] | Hernando A, Navarro I, Gorria P. Phys Rev, 1995, 51B:3281 |
| [6] | Hono K, Li J L, Inoue A, Sakurai T. Appl Surf Sci, 1993,67:398 |
| [7] | Lin D M, Wang H S, Wu Y C, Lin M L. Chin Phys, 1999,8:455 |
| [8] | Shao Y Z, Lin G M, Lan T, Zhong W R. Acta Phys Sin,2002, 51:2362(邵元智,林光明,蓝图,钟伟荣.物理学报,2002,51:2362) |
| [9] | Herzer G. IEEE Trans Mag, 1990, 26:1397 |
| [10] | Ji S, Yang G B, Wang R. Acta Phys Sin, 1996, 45:2061(纪松,杨国斌,王润.物理学报,1996,45:2061) |
| [11] | Liu T, Xu Z X, Zhao Z T, Ma R Z, Hu T D, Xie Y N,Guo Y H. Sci Chin, 1996, 26A: 1015(刘涛,徐祖雄,赵钟涛,马如璋,胡天斗,谢亚宁,郭应焕.中国科学,1996,26:1015) |
| [12] | Shek C H, Shao Y Z, Lai J K L. Phys, 2000, 276A: 201 |
| [13] | Pei W G, Zhong W L, Yue S B. X-ray Diffraction of Mono-Crystal, Multi-Crystal and Amorphous Material,Jinan: Publishing house of Shandong University, 1986:331(裴文光，钟维烈，岳书彬.单晶、多晶和非晶物质的X射线衍 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%