应用ANSYS软件对具有复合组织的电磁离心铸造1Crl8Ni9Ti不锈钢管的周期轧制过程进行了三维有限元数值模拟.模拟结果表明,管坯轴向塑性越好,在轧制过程中产生的剪切应力σrz和剪切应变εrz越小,管坯变形能力越强.降低工具与管坯摩擦系数,可以减小σrz和εrz,减小管坯外层柱状晶区与内层等轴晶区之间σrz的不连续性,提高管坯的变形能力和成形管材的质量.在电磁离心凝固时适当地加大励磁电流以增加铸管中等轴晶区比例,不但可以提高铸管的力学性能,还可以减小管坯在轧制过程中所产生的σrz和εrz,进而使其轧制变形能力增强,其成形管材质量也得到改善.通过轧制实验验证,模拟结果与实验结果吻合良好.
参考文献
| [1] | Yang Y S, Liu Q M, Jiao Y N, Ge Y L, Hu Z Q, Gao Y Y, Jia G L, Zhang G Z. ISIJ Int, 1995; 35(4): 389 |
| [2] | Wu X Q, Yang Y S, Hui X D, Hu Z Q. Scandinavian J Metall, 1999; 28:59 |
| [3] | Yang Y S, Hu Z Q. Z Metallkd, 2001; 91(4): 280 |
| [4] | Guo M H, Yang Y S, Hua F A, Guo D Y, He Y L, Hu Z Q. J Mater Eng, 2002; 232(9): 7(郭明虎,杨院生,花福安,郭大勇,贺幼良,胡壮麒.材料工程,2002;232(9):7) |
| [5] | Yang Y S, Zhe W X, Hu Z Q. Proceedings of PRICM4,2001; 349 |
| [6] | Lin G, Yang Y S, Hua F A, Guo D Y, Hu Z Q. Acta Metall Sin, 2003; 39:1232(林刚,杨院生,花福安,郭大勇,胡壮麒.金属学报,2003;39:1232) |
| [7] | Mulot S, Hacquin A, Montmitonnet P, Aubin J L. J Mater Proc Technol, 1996; 60:505 |
| [8] | Montmitonnet P, Loge R, Hamery M, Chastel Y, Doudoux J L, Aubin J L. J Mater Proc Technol, 2002; 125-126:814 |
| [9] | Su D. The Mechanical Property of Metal. Beijing: China Machine Press, 1987:74(束德林.金属力学性能.北京:机械工业出版社,1987:74) |
| [10] | Hill R A. Proc R Soc London, Ser. 1948; B193:281 |
| [11] | Girard E, Guillen R, Weisbecker P, Francois M. J Nuclear Mater, 2001(294): 330 |
| [12] | Cockctoft M G, Latham D J. A Simple Criterion of Ftacture for Ductile Metals. National Engineering Laboratory.Report Number 240, 1966 |
| [13] | Cockctoft M G, Latham D J. J Inst Metals, 1968; 96:33 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%