多道富锌基涂层的电化学行为研究表明,涂层中的Zn粉未表现出明显的阴极保护作用,即使在富锌涂层上覆盖几个微米厚的环氧清漆涂层,Zn的阴极保护作用也会变得非常微弱.Zn粉对钢铁的保护作用在于Zn粉腐蚀产物对涂层的"自修复能力".在环氧清漆覆盖条件下,无机富锌涂层中Zn粉的反应活性比有机富锌涂层中Zn粉的高,即Zn粉的反应速度更快.
参考文献
| [1] | Feliu S, Barajas R, Bastidas J M, Morcillo M. J Coat Technol, 1989; 61(775): 63 |
| [2] | Feliu S, Barajas R, Bastidas J M, Morcillo M. J Coat Technol, 1989; 61(775): 71 |
| [3] | Abreu C M, Izquierdo M, Keddam M, Novoa X R, Takenouti H. Electrochimica Acta, 1996; 41:2405 |
| [4] | Abreu C M, Izquierdo M, Merino P, Novoa X R, Perez C.Corros,1999; 55:1173 |
| [5] | Feliu S Jr, Morcillo M, Feliu S. Corros, 2001; 57(7): 591 |
| [6] | Morcillo M, Barajas R, Feliu S, Bastidas J M. J Mater Sci, 1990; 25(5): 2441 |
| [7] | Di Sarli A R, Cavalcanti E, Ferraz O. Corros Prevent &Control, 1993; 40(3): 66 |
| [8] | Mansfeld F, Xiao H, Han L T, Lee C C. Prog Org Coat,1997; 30(1-2): 89 |
| [9] | Almeida E, Santos D, Uruchurtu J. Prog Org Coat, 1999;37(3-4): 131 |
| [10] | Morris W, Vazquez M, De Sanchez S R. J Mater Sci, 2000;35(8): 1885 |
| [11] | Liang F, Zhang J Q, Liu H W, Xu S Q, Cao C N, Lin H C, Dong J L, Cai Z Y. Chin Soc Corros Prot, 1993; 13(1):70(梁峰,张鉴清,刘宏伟,许淑琴,曹楚南,林海潮,董建梁,蔡兆英.中国腐蚀与防护学报,1993;13(1):70) |
| [12] | Harayama S, Asari S, Tsuru T. J Electrochem Soc, 1987;87(2): 197 |
| [13] | Liu H W, Dong J L. Corros Sci Prot Technol, 1992; 4(3):144(刘宏伟,董建梁.腐蚀科学与防护技术,1992;4(3):144) |
| [14] | Scully J R, Hensley S T. Corros, 1994; 50(9): 705 |
| [15] | Hu J M, Xie D M, Zhang J Q, Cao C N. Chin Soc Corros Prot, 2002; 22(5): 311(胡吉明,张鉴清,谢德明,曹楚南.中国腐蚀与防护学报,2002;22(5):311) |
| [16] | Cerisola G.Mater Chem, 1982; 7(2): 241 |
| [17] | Leidheiser H Jr. Prog Org Coat, 1979; 7:79 |
| [18] | Leidheiser H Jr. J Coat Technol, 1991; 63(802): 21 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%