用直流磁控溅射方法制备了性能优良的以(Ni0.81Fe0.19)1-xCrx为种子层的Ni0.81Fe0.19薄膜,研究了种子层成分及厚度对薄膜磁性和微结构的影响,结果表明:当种子层(Ni0.81Fe0.19)0.63Cr0.37厚度为5.5 nm时,Ni0.81Fe019(20.0 nm)薄膜的各向异性磁电阻(AMR)值为(2.53±0.06)%;当Cr的含量为0.36时,Ni0 81Fe0.19(60.0 nm)薄膜的AMR值为(3.35±0.06)%.AFM及XRD研究表明:不同厚度缓冲层(厚度分别为2.8,5.5和8.3 nm)的Ni0.81Fe0.19(20.0 nm)薄膜表面平均晶粒尺寸基本都为35.2 nm,但其111织构相差很大,AMR值最大时,对应的111衍射峰最强;不同Cr含量(分别为0.28,0.36和0.41)的Ni0.81Fe0.19(60.0 nm)薄膜表面平均晶粒尺寸和111衍射峰相差都很明显,AMR值最大时,对应地薄膜表面平均晶粒尺寸最大,Ni0.81Fe0.19111衍射峰也最强.

参考文献

[1] Tsang C, Decker S. J Appl Phys, 1981: 52:2645
[2] Tsang C, Lin T, MacDonald S. IEEE Trans Magn, 1997:33:2866
[3] Mcguire T R, Potter R I. IEEE Trans Magn, 1975: 11: 1018
[4] Aker M A, Mapps D J, Ma Y Q. J Appl Phys, 1997: 81: 4122
[5] Aker M A, Mapps D J, Ma Y Q. IEEE Trans Magn, 1998:34:1147
[6] Miyazaki T, Ajima T, Sato F. J Magn Magn Mater, 1989:81:86
[7] Funaki H, Okamoto S, Kitakami O. J Appl Phys, 1994: 33:1304
[8] Lee W Y, Toney M F, Mauri D. IEEE Trans Magn, 2000: 36:381
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%