用粉末冶金方法制备了一种以三元层状陶瓷Ti2SnC为增强相的Cu/Ti2SnC复合材料,研究了增强相的含量对复合材料的显微结构和硬度、拉伸强度等力学性能的影响.结果表明,Ti2SnC对于铜是一种有效的增强相,当Ti2SnC的体积含量为20%(体积分数,下同)时增强效果最佳,屈服强度和拉伸强度分别达到319 Mpa和440 Mpa,是相同工艺条件下制备的纯铜的屈服强度和拉伸强度的4倍和2倍,并保持12%的延伸率.强化是由于铜基体晶粒的细化和位错塞积引起的.
参考文献
| [1] | Groza J R, Gibeling J C. Mater Sci Eng, 1993; A171:115 |
| [2] | Zhou Y C, Sun Z M, Sun J H, Zhang Y, Zhou J. Z Metallkd, 2000; 91:329 |
| [3] | Wang X H, Zhou Y C. J Mater Chem, 2002; 12:455 |
| [4] | Zhou Y C, Dong H Y. Mater Res Innovat, 2000; 4:36 |
| [5] | Dong H Y, Yah C K, Chen S Q, Zhou Y C. J Mater Chem,2001; 11:1402 |
| [6] | Zhang Y, Sun Z M, Zhou Y C. Mater Res Innovat, 1999;3:80 |
| [7] | Zhang Y, Zhou Y C. Z Metallkd, 2000; 92:585 |
| [8] | Petch N J. J Iron Steel Inst, 1953; 174:25 |
| [9] | McElroy R J, Szkopiak Z C. Int Met Rev, 1972; 17:175 |
| [10] | Zhang Y, Zhou Y C. Acta Metall Sin, 2000; 36:662(张毅,周延春.金属学报,2000;36:662) |
| [11] | Arsenault R J, Shi N. Mater Sci Eng, 1986; 86:175 |
| [12] | Hansen N. Acta Metall, 1977; 25:863 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%